Abstract:Single crystals of SrAl2O4 prepared with 0.2–2.0 mol% Eu2O3 were synthesized using the optical floating zone method using ceramic rods that had been prepared under reducing conditions to favor conversion of Eu3+ to Eu2+. Samples were then characterized by a combination of X-ray diffraction (XRD), X-ray photoelectron (XPS), positron annihilation, electron paramagnetic resonance (EPR), photoluminescence excitation (PLE) and photoluminescence (PL) spectroscopic techniques, and their excited state lifetimes were measured. XRD showed that the crystal samples were all in the monoclinic phase. EPR and PL techniques indicated that they contained Eu2+, although XPS indicated that the Eu3+ reduction was only ∼50%. Positron annihilation spectroscopy demonstrated that all of the samples contained a considerable number of defects that act as positron traps, and were influenced by the amount of Eu2O3 used in the crystal synthesis. These defects did not show an EPR signal, which suggests that they may correspond structural vacancies, possibly due to the presence of cation vacancies as a result of incorporation of some Eu3+ in the divalent cation sites. However, EPR did reveal a small amount of anionic paramagnetic defects, and showed a progressive broadening of the Eu2+ resonance for crystals synthesized with Eu2O3 concentrations >0.5 mol%. The intensity of the PLE spectra increased with Eu2O3 concentration, and the relative proportions of the peaks at 3.62 eV (360 nm) and 3.13 eV (417 nm) changed with Eu2O3 concentration. The PL spectra showed a broad green emission peak at 2.52 eV (518 nm), which is attributed to 4f65d-4f7 charge transfer transitions in Eu2+. Both its intensity and fluorescence decay time increased with Eu2O3 concentration, reached a maximum with the sample prepared with 1.5 mol% Eu2O3, then decreased with higher Eu2O3 concentrations.

Mechanoluminescence of Persistent Luminescent Sral2o4: (eu2+, Dy3+) Material Prepared by Electron Beam Reduction

Investigation of the Long Afterglow Mechanism in SrAl2O4:Eu2+/Dy3+ by Optically Stimulated Luminescence and Thermoluminescence

Warm-white Persistent Luminescence of Lu3Al2Ga3O12:Pr3+ Phosphor

Luminescent Properties of Sral2o4 : Eu, Dy Material Prepared by the Gel Method

Preparation of long-afterglow Sr4Al14O25-based luminescent material and its optical properties

Stimulus response of mechanoluminescence of SrAl 2 O 4 :Eu,Dy mixed with epoxy resin using uniaxial load

Persistent Luminescence of Sral2o4: Eu2+, Dy3+, Cr3+ Phosphors in the Tissue Transparency Window

Studies on Mechanoluminescence from SrAl2O4:Eu, Dy Phosphor

Anomalous Luminescence in Sr4al14o25 : Eu, Dy Phosphors

Fabrication and characterizations of Eu2+‐Dy3+ co‐doped SrAl2O4 ceramics with persistent luminescence

Defects and persistent luminescence in Eu-doped SrAl$_2$O$_4$

Mechano-luminescence of Eu 2+ , Dy 3+ co-doped strontium aluminate phosphors with the substitution of calcium ions

Synthesis, structure, and luminescence properties of SrSiAl<sub>2</sub>O<sub>3</sub>N<sub>2</sub>:Eu<sup>2+</sup> phosphors for light-emitting devices and field emission displays

PREPARATION OF ULTRAFINE SrAl2O4-BASED LUMINESCENT MATERIAL DOPED WITH RARE EARTH IONS AND THEIR OPTICAL PROPERTIES

Luminescence and microstructural characteristics of Eu2O3-doped SrAl2O4 single crystals

Long afterglow luminescence mechanism of SrAl2O4-based phosphor by the thermoluminescence and positron annihilation method

PREPARATION OF ULTRAFINE SrAl_O_4-BASED LUMINESCENT MATERIAL DOPED WITH RARE EARTH IONS AND THEIR OPTICAL PROPERTIES

The long rod‐shaped Sr2MgSi2O7:Eu2+,Dy3+ with ultrahigh afterglow performance

Luminescent Properties Of Blue-Emitting Long Afterglow Phosphors Sr2-Xcaxmgsi2o7 : Eu2+, Dy3+ (X=0, 1)

Sol-Gel Synthesis of Translucent and Persistent Luminescent SiO2@ SrAl2O4 Eu, Dy, B Materials

Photoluminescence and Thermal Stability of Β-Sialon:Re (re = Sm, Dy) Phosphors