Crystal Structure and Luminescent Property of Flaky-Shaped Sr4al14o25:Eu2+, Dy3+ Phosphor Doped with Er3+ Ions
Fengfeng Li,Zhihong Li,Xiaomin Wang,Mingxi Zhang,Yi Shen,Pan Cai,Xinyu He
DOI: https://doi.org/10.1016/j.jallcom.2016.07.195
IF: 6.2
2017-01-01
Journal of Alloys and Compounds
Abstract:In this study, the afterglow properties of Sr4Al14O25: Eu2+, Dy3+ was successfully improved and the absorption in the visible region (> 400 nm) was increased using co-doped Er3+ ions, thus facilitating the application of Sr4Al14O25: Eu2+, Dy3+ in daylight environment. A series of Sr3.88-xAl14O25:0.04Eu(2+), 0.08Dy(3+), xEr(3+) (x = 0, 0.04, 0.08, 0.12, 0.16, and 0.20) phosphors were prepared using a conventional high-temperature solid-phase method; their structures were characterized by XRD, TEM, HRTEM, FT-IR, and XPS. The luminescence properties, with excitation at 275 nm and 360 nm, were systematically compared and analyzed by fluorescence spectra, afterglow spectra, and afterglow decay spectra. Interestingly, although the Er3+ doping slightly affected the crystal structure of Sr4Al14O25: Eu2+, Dy3+ phosphor, the luminescent properties of phosphors were affected to a large extent. After the Er3+ doping, the emission peak of Eu2+ at 485 nm split into three peaks at 481 nm, 492 nm, and 529 nm. An appropriate Er3+ doping significantly enhanced the afterglow performance of the phosphors, whereas excessive Er3+ doping caused concentration quenching. The absorption in the visible region (> 400 nm) increased with Er3+ doping, which was more suitable for the application of Sr4Al14O25: Eu2+, Dy3+ in daylight environment. The initial afterglow intensities with 360 nm excitation were higher than those with 275 nm excitation, whereas the afterglow time of the former was slightly shorter than that of the later. The one-dimensional and two-dimensional lattice fringe phase of the local particles can be observed clearly from HRTEM of flaky-shaped Sr3.76Al14O25: 0.04Eu(2+), 0.08Dy(3+), 0.12Er(3+) particle, which was rare in the previous reports. Moreover, the preliminarily enhancing mechanism of Er3+ on the luminescent properties of Sr3.88Al14O25: 0.04Eu(2+), 0.08Dy(3+) phosphor was analyzed. (C) 2016 Elsevier B.V. All rights reserved.