Design, processing, 3D/4D printing, and characterization of the novel PETG–PBAT blends
Saeed J. A. Ali,Davood Rahmatabadi,Mostafa Baghani,Majid Baniassadi
DOI: https://doi.org/10.1007/s10853-024-09761-8
IF: 4.5
2024-05-29
Journal of Materials Science
Abstract:In this article, we conducted a study on the design, processing, 3D/4D printing, and characterization of mechanical properties, thermomechanical properties, printability, morphology, and shape memory performance of the novel PETG–PBAT blends. For this purpose, polyethylene terephthalate glycol (PETG)–polybutylene adipate terephthalate (PBAT) blends with three weight percentages of 10, 20, and 30 PBAT were prepared using melt mixing. After undergoing various stages, granules were obtained for 3D printing. The 3D printing was done using the granule-based material extrusion method equipped with a pneumatic system to direct the melt flow to the nozzle, and this method made the conditions of controlling and manipulating the melt flow easier to achieve ideal and uniform printing. The results of the thermomechanical and morphological investigations indicated that the PETG–PBAT was immiscible with proper compatibility of the two phases. This issue was also effective in achieving excellent mechanical properties and printability. Tensile strength and elongation increased and decreased, respectively, with increasing PBAT. The PBAT10% had a tensile strength of 36 MPa and an elongation of 51%, which is great compared to fused deposition modeling 3D printing material library. The proper compatibility of the two phases, the excellent printability due to the control of the output melt flow and the selection of the printing parameters were the reasons for achieving excellent mechanical properties. Despite the low printability, the PBAT30% sample showed more than 100% elongation and good toughness. The results of the shape memory performance demonstrated that with the increase in the PBAT due to the reduction in the transition temperature and the strengthening of the elastic part, a higher shape recovery was achieved at a faster rate.
materials science, multidisciplinary