Effects of solution treatment on microstructures and properties of Al-8.54Zn-2.41Mg-xCu aluminum alloys

孔晓华,陈康华,董朋轩,陈送义
DOI: https://doi.org/10.3969/j.issn.1673-0224.2014.03.007
2014-01-01
Abstract:The effects of solution treatment on the microstructures and properties of Al-8.54Zn-2.41Mg-xCu alloys was studied by OM, SEM, room temperature tensile test and electrochemical corrosion test. The results show that the amount of residual phases decreases rapidly, the volume fraction of recrystallization increases and the polarization curves move to positive direction with increasing solution time. When the solution time is 60 min, the strength and the resistance to corrosion of the alloy with 1.3%(mass fraction)copper content are better than those of the alloy with 2.2%copper content. When the solution time increases to 180 min, the tensile strength and yield strength of the alloy with 2.2%copper content increase slightly and those of the another alloy decrease;the exfoliation corrosion degree of the alloy with 1.3%copper is higher than that of the alloy with 2.2%copper content, and its resistance to corrosion is better than the alloy with lower copper content. It is also found that appropriately decreasing the solution time can improve the strength and the corrosion resistance of the alloy with low copper content. The corrosion potential of the alloys has little difference, when copper content is lowered within a certain range.
What problem does this paper attempt to address?