Mechanical alloying of Mo—Si—Fe powders

曹昱,易丹青,张松
IF: 3.752
2002-01-01
Transactions of Nonferrous Metals Society of China
Abstract:Mechanical milling behavior of Mo-Si-Fe powders was investigated using XRD, SEM and TEM techniques. The mixtures of elemental molybdenum (>99%), silicon (>99%) andiron (>98%) powders with a stoichiometry of Mo5-xFexSi3(x = 0.5, 1, 2) were milled in a planetary mill for up to 195 h. For all three powder mixtures, high-energy milling of 60 h led to formation of the Mo(Fe, Si) supersaturated solid solution (Mo-ss); and to a remarkable expansion of the solubility of Fe, Si in molybdenum. The transformation of Mo-ss to an amorphous phase was identified after longer time milling. In the milling process, the grain size of Mo (Fe, Si) decreased gradually and the internal stress increased linearly. After 40 h milling, the grain size was reduced to about 11 nm. SEM analysis of milled powders showed that the particle size increased initially with milling time. After 195 h milling, particles exhibited a spherical morphology and the particle size were reduced to about 100 nm.
What problem does this paper attempt to address?