Abstract:Pt/CeO2 catalysts with nanoporous structures were prepared by the facile dealloying of melt-spun Al92-XCe8PtX (X = 0.1; 0.3 and 0.5) ribbons followed by calcination. The phase compositions and structural parameters of the catalysts were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and high-resolution transmission electron microscopy (HRTEM). The specific surface area and pore size distribution were characterized by N-2 adsorption-desorption tests. The catalytic properties were evaluated by a three-way catalyst (TWC) measurement system. The results revealed that the dealloyed samples exhibited a nanorod framework structure. The Pt nanoparticles that formed in situ were supported and highly dispersed on the CeO2 nanorod surface and had sizes in the range of 2-5 nm. For the catalyst prepared from the melt-spun Al91.7Ce8Pt0.3 ribbons, the 50% CO conversion temperature (T-50) was 91 degrees C, and total CO could be converted when the temperature was increased to 113 degrees C. An X-ray photoelectron spectroscopy (XPS) test showed that the Pt-0.3/CeO2 sample had a slightly richer oxygen vacancy; and a H-2 temperature-programmed reduction (H-2-TPR) test demonstrated its superior adsorption ability for reduction gas and high content of active oxygen species. The experiments indicated that the catalytic performance could be retained without any attenuation after 130 h when water and CO2 were present in the reaction gas. The favorable catalytic activities were attributed to the high specific areas and small pore and Pt particle sizes as well as the strong interactions between the CeO2 and Pt nanoparticles. The Pt nanoparticles were embedded in the surface of the CeO2 nanorods, inhibiting growth. Therefore, the catalytic stability and water resistance were excellent.

Monodisperse, Nanoporous Ceria Microspheres Embedded with Pt Nanoparticles: General Facile Synthesis and Catalytic Application

Trimetallic PtPdCo Mesoporous Nanopolyhedra with Hollow Cavities

Embedding Ultrafine and High-Content Pt Nanoparticles at Ceria Surface for Enhanced Thermal Stability.

Mesoporous-shelled CeO2 hollow nanospheres synthesized by a one-pot hydrothermal route and their catalytic performance

Hierarchical Nanospheres Based on Pd Nanoparticles Dispersed on Carbon Coated Magnetite Cores with A Mesoporous Ceria Shell: A Highly Integrated Multifunctional Catalyst

Aqueous‐Phase Synthesis of Pt/CeO2 Hybrid Nanostructures and Their Catalytic Properties

Facile Synthesis of Ceria Nanocrystals with Tuneable Size and Shape

Mesoporous SiO2-Supported Pt Nanoparticles for Catalytic Application

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

Mesoscale organization of nearly monodisperse flowerlike ceria microspheres.

Homogeneously Dispersed Ceria Nanocatalyst Stabilized with Ordered Mesoporous Alumina

A Versatile Designed Synthesis Of Magnetically Separable Nano-Catalysts With Well-Defined Core-Shell Nanostructures

Smart Design Of Small Pd Nanoparticles Confined In Hollow Carbon Nanospheres With Large Center-Radial Mesopores

Pt-embedded-CeO2 hollow spheres for enhancing CO oxidation performance

A General and Feasible Method for the Fabrication of Functional Nanoparticles in Mesoporous Silica Hollow Composite Spheres

Multifunctional Mesoporous Composite Microspheres with Well-Designed Nanostructure: a Highly Integrated Catalyst System.

Controlled Synthesis of Sintering-Resistant Pd@CeO2 Core–Shell Nanotube Catalysts for CO Oxidation

Strongly Coupled Pt-Ni2geo4 Hybrid Nanostructures As Potential Nanocatalysts for Co Oxidation

Dimension-Manipulated Ceria Nanostructures (0d Uniform Nanocrystals, 2d Polycrystalline Assembly, and 3d Mesoporous Framework) from Cerium Octylate Precursor in Solution Phases and Their Co Oxidation Activities

Preparation of uniform magnetic recoverable catalyst microspheres with hierarchically mesoporous structure by using porous polymer microsphere template

The Preparation And Catalytic Properties Of Nanoporous Pt/Ceo2 Composites With Nanorod Framework Structures