Mesoporous SiO2-Supported Pt Nanoparticles for Catalytic Application

yingze cao,wentao zhai,xiang zhang,shuxi li,lin feng,yen wei

DOI: https://doi.org/10.1155/2013/745397

2013-01-01

Abstract:SiO2 nanoparticles have been synthesized by combining Stober’s method and nonsurfactant process. The diameters and pore sizes can be controlled by altering the template and its concentration. Mesoporous SiO2 obtained this way has extremely large surface area compared with most oxide supports, which benefits the catalytic performance. Pt nanoparticles were in situ grown on and in mesoporous SiO2 nanoparticles with low amount of the metal and high load ratio. Furthermore, we firstly developed a novel route, called “one-pot” method, to prepare Pt/SiO2 catalyst where mesoporous silica preparing and Pt loading occurred in one step. This method is more efficient in saving reagent, since it can prevent Pt loss. In the meantime, it enables the template to reduce agent. The catalytic activity of Pt/SiO2 samples was measured by CO oxidation. It is indicated that the supporting silica with mesopores is more active than silica with micropores.