Abstract:Alkane aromatization is a significant supplementary route for the preparation of value-added aromatic products. Although ZSM-5 zeolites have been widely used in alkanes aromatization, they always exhibit low catalytic stability, due to the diffusion limitation of medium-pore structure, resulting in rapid deactivation. Moreover, the excessive strong acid sites of ZSM-5 also induce serious cracking reaction. To overcome these issues, the pore structure and acidic property of ZSM-5 zeolite were controllably regulated using ammonium hexafluorosilicate (AHFS) and potassium carbonate (K2CO3) post-treatment method. After loading Pt, the Pt/KZSM-5(deAl) catalyst showed aromatic selectivity as high as 75.4%, with n-heptane conversion of 96.1%, at 550 °C and ambient pressure. More importantly, the catalytic lifetime reached 234 h. Even for the aromatization of n-octane and n-nonane with larger molecular size, the Pt/KZSM-5(deAl) still gave high aromatic selectivity of 82.7% and 83.4%, and n-octane and n-nonane conversion of 92.8% and 87.1%, along with the catalytic lifetime higher than 80 h. The results of XRD, N2 sorption, NH3-TPD, Py-IR, TEM/STEM, H2-TPR, CO-DRIFT and XPS indicated that using AHFS and K2CO3 post-treatment can not only produce more mesoporous to facilitate the diffusion of aromatic products, but also reduce the amount and strength of strong acid sites in ZSM-5 to avoid the over-cracking reaction. Moreover, the generated defect sites due to dealumination and the residual potassium ions (K+) on zeolite enhanced the interaction between Pt and ZSM-5 zeolite that effectively suppresses the aggregation and sintering of Pt particles.

Enhanced Catalytic Activity in Propene Oxidation over NaZSM-5 Zeolite-Supported Pt Nanoparticles by Increasing the Zeolite Si/Al Ratio

Phosphorous Modified High Silica ZSM-5 Spherical Catalyst and Its Reaction on Methanol to Propylene

Effect of Si/Al ratio on performance of Pt–Sn-based catalyst supported on ZSM-5 zeolite for n-butane conversion to light olefins

Influence of Operating Conditions, Si/Al Ratio and Doping of Zinc on Pt-Sn/ZSM-5 Catalyst for Propane Dehydrogenation to Propene

Effect of the Si/Al Ratios of Nanocrystalline HZSM-5 Zeolite on the Performance in Catalytic Conversion of Ethanol to Propylene

Propene and CO Oxidation on Pt/Ce-Zr-SO 4 2– Diesel Oxidation Catalysts: Effect of Sulfate on Activity and Stability

Catalytic Study of Methanol-to-Propylene Conversion over Nano-Sized HZSM-5

Anatase‐reinforced PtZn@Silicalite‐1 Structured Catalysts Boosting Propane Dehydrogenation

Regulation of framework Al distribution of high-silica hierarchically structured ZSM-5 zeolites by boron-modification and its effect on materials catalytic performance in methanol-to-propylene reaction

Bimetallic PtZn nanoparticles anchored in high-silica SSZ-13 zeolite for efficient propane dehydrogenation

Catalytic cracking of C4 alkenes to propene and ethene: Influences of zeolites pore structures and Si/Al2 ratios

Hydrophobic Modification of Zeolite-Supported Platinum Catalysts for Complete Oxidation of Toluene

Direct synthesis of HZSM-5 zeolites with enhanced catalytic performance in the methanol-to-propylene reaction

Excellent catalytic performance over hierarchical ZSM-48 zeolite: Cooperative effects of enhanced mesoporosity and highly-accessible acidity

Low-content Pt loading on a post-treatment-free zeolite for efficient catalytic combustion of toluene

ZnO supported on high silica HZSM-5 as new catalysts for dehydrogenation of propane to propene in the presence of CO2

Subnanometer Bimetallic Platinum-Zinc Clusters in Zeolites for Propane Dehydrogenation

New insight into seeding process leading to improved zeolitic acidity and surface properties for its catalytic application in propane aromatization

Role of Al in Na-ZSM-5 zeolite structure on catalyst stability in butene cracking reaction

Aromatization of n-C7 ~ n-C9 Alkanes on Pt/KZSM-5(deAl) Catalyst

Highly Efficient Oxidation of Propane at Low Temperature over a Pt-Based Catalyst by Optimization Support