Misorientation effect of grain boundary on the formation of discontinuous precipitation in second and third generation single crystal superalloys

zhengrong yu,xianfei ding,yunrong zheng,lamei cao,qiang feng
DOI: https://doi.org/10.1051/matecconf/20141411006
2014-01-01
MATEC Web of Conferences
Abstract:[001] tilt artificial grain boundaries of Ni-based single crystal superalloys CMSX-4 and DD10 have been prepared by self-diffusion bonding. The microstructural stability of 0 similar to 30 degrees artificial grain boundaries have been investigated after heat treatment at 1100 degrees C for 0 similar to 300 h. TCP phases and cellular colony developed on boundaries are related to misorientation angle of the bonded boundaries of DD10 and DD10 alloys as well as the bonded boundaries of CMSX-4 and DD10 alloys. The heterogeneous nucleation of TCP phase, enveloped by gamma' film, occurred along 15 degrees and 20 degrees boundaries. Discontinuous Precipitation (DP) reaction occurred along high misorientation angle (20 degrees similar to 30 degrees) boundaries. However, no TCP phase formation existed along grain boundaries with different misorientation angles in CMSX-4/CMSX-4 bonded alloys as well as for a 0 degrees boundary in DD10/DD10 and CMSX-4/DD10 bonded alloys. The current study clearly suggests that grain boundary precipitation and its morphology were influenced by the misorientation angle of grain boundary and the content of refractory elements in alloy.
What problem does this paper attempt to address?