Synthesis and Magnetic Properties of Mnb2o6 (M = Fe, Co, Ni) Nanoparticles

Shuijin Lei,Chuanning Wang,Donghai Guo,Xijie Gao,Di Cheng,Jianliang Zhou,Baochang Chenga,Yanhe Xiao
DOI: https://doi.org/10.1039/c4ra08269a
IF: 4.036
2014-01-01
RSC Advances
Abstract:Considerable efforts have been exerted on the controllable synthesis of columbite niobate ceramics due to their fascinating properties and applications. Especially, it is still a great challenge to fabricate nanostructures of the niobate series. In this research, FeNb2O6, CoNb2O6 and NiNb2O6 nanoparticles have been successfully prepared via a facile hydrothermal route followed by heat treatment. X-ray powder diffraction patterns show that all the products have the typical orthorhombic columbite structure. The electron microscopy analyses reveal that the obtained nanoparticles have diameters of 50-100 nm. The magnetic property results demonstrate that the magnetically ordered state is hard to observe down to 1.8 K for the FeNb2O6 sample, while the magnetic transition temperatures of T-N = 3 K and T-N = 6 K can be obtained for CoNb2O6 and NiNb2O6 samples, respectively. A weak ferromagnetic moment can be detected below 5 K for both CoNb2O6 and NiNb2O6 samples. Furthermore, the NiNb2O6 sample even exhibits a metamagnetic transition at 1.8 K due to the spin flipping of the ferromagnetic chains.
What problem does this paper attempt to address?