Abstract:Tungsten oxide (WO3) is a strong candidate as the photoanode in photoelectrochemical (PEC) water splitting owing to its moderate band gap (2.6–3.2 eV) for wide light absorption and stable physicochemical properties. This work reports a morphology engineering strategy to fabricate voltage-induced terrace-like tungsten oxide (TW) film and its high-voltage performance as a photoanode for PEC water splitting. By controlling the anodization voltage, the morphology of the anodic WO3 film was altered, and their photoelectrochemical performances were compared. Anodization of the tungsten film in fluoride-containing H3PO4 leads to the growth of either irregular porous tungsten oxide layers or terrace-like tungsten oxide layers, depending on the anodic potentials. The possible growth mechanism of the porous oxide layer during anodization is proposed with a combination of the field-assisted dissolution model and the oxygen-bubble mold model. Under light irradiation, the photocurrent density was 3.0 mA cm–2 at 1.23 V vs RHE (VRHE) for annealed terrace-like WO3, which was almost 3 times larger than that of annealed porous WO3. As a photoanode, terrace-like WO3 films could generate hydrogen at 58 μmol cm–2 h–1 under simulated solar light, while porous WO3 films produced hydrogen with a slower rate of 28 μmol cm–2 h–1. The terrace-like WO3 films experience higher photoelectrochemical performance and incident photon-to-electron conversion efficiency (IPCE) than porous WO3 due to more regular nanostructure, smaller band gap, fast charge-transfer rate, and alleviated recombination rate. This study shows that morphology control can effectively enhance the photocurrent density and IPCE of photoanodes and suggests a practical direction for finding the optimal WO3 films for PEC water splitting.

Preparation of well-aligned WO 3 nanoflake arrays vertically grown on tungsten substrate as photoanode for photoelectrochemical water splitting

Seed Layer-Free Hydrothermal Synthesis of Porous Tungsten Trioxide Nanoflake Arrays for Photoelectrochemical Water Splitting.

Facile Fabrication of Sandwich Structured WO3 Nanoplate Arrays for Efficient Photoelectrochemical Water Splitting.

Porous Ultrathin WO3 Nanoflake Arrays As Highly Efficient Photoanode for Water Splitting

Preparation of Vertically Aligned WO3 Nanoplate Array Films Based on Peroxotungstate Reduction Reaction and Their Excellent Photoelectrocatalytic Performance

Wo3 Nanoflakes for Enhanced Photoelectrochemical Conversion

Preparation and characterization of a novel WO_3/W photoanode

Cuwo4 Nanoflake Array-Based Single-Junction and Heterojunction Photoanodes for Photoelectrochemical Water Oxidation

Enhanced Photoelectrochemical Water Splitting on Novel Nanoflake WO3 Electrodes by Dealloying of Amorphous Fe–W Alloys

High-Voltage Etching-Induced Terrace-like WO 3 Photoanode for Efficient Photoelectrochemical Water Splitting

Large-Scale Tunable 3D Self-Supporting WO3 Micro-Nano Architectures As Direct Photoanodes for Efficient Photoelectrochemical Water Splitting.

Efficient Photoelectrochemical Water Splitting and Impedance Analysis of WO3−x Nanoflake Electrodes

Synthesis of WO3@ZnWO4@ZnO-ZnO Hierarchical Nanocactus Arrays for Efficient Photoelectrochemical Water Splitting

Facile Synthesis of Ni-doped WO3 Nanoplate Arrays for Effective Photoelectrochemical Water Splitting

Tungsten oxide nanostructures and nanocomposites for photoelectrochemical water splitting

Effective Silicon Nanowire Arrays/wo3 Core/shell Photoelectrode for Neutral Ph Water Splitting

Controllable synthesis of vertically aligned WO3 nanoplate arrays on stainless steel for improved visible-light photoelectrocatalytic activity

Nanoporous WO3 Films Synthesized by Tuning Anodization Conditions for Photoelectrochemical Water Oxidation

Self‐Assembled Urchin‐Like CuWO 4 /WO 3 Heterojunction Nanoarrays as Photoanodes for Photoelectrochemical Water Splitting

WO3 Nanoflakes Decorated with CuO Clusters for Enhanced Photoelectrochemical Water Splitting

3D hierarchical WO3 grown on TiO2 nanotube arrays and their photoelectrochemical performance for water splitting