Abstract:The microstructures and mechanical behavior of the as-cast and isothermally annealed Zr(63)Al(9.7)Ni(9.7)Cu(14.6)Nb(3) bulk metallic glasses (BMGs) were studied by differential scanning calorimetry (DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), and room temperature uniaxial compression. The as-cast BMG alloy shows a wide undercooled liquid span of 73 K at a constant heating rate of 40 K/min. Composite microstructures containing nanometer scaled icosahedral quasicrystals (i-phase) were produced upon annealing at 705 K. Under uniaxial room-temperature compression at a strain rate of 5x10(-4) s(-1), the as-cast BMG alloy exhibits a elastic deformation epsilon(y) similar to 1.95%, a yield stress sigma(y) similar to 1650 MPa, and a Young's modulus E similar to 84.5 GPa. The alloy shows a plastic strain epsilon(p) similar to 8.0 % in a serrated plastic deformation process. Annealing induced embrittlement was observed in the relaxed BMG alloys. Comparing with the as-cast alloy, the relaxed and the composite alloys show negligible changes in elastic strain and Young's modulus. The partially crystallized alloys are macroscopically brittle. Well developed vein patterns were observed in the fracture surfaces of all these alloys. The present work revealed that the dispersion of nanometer scaled i-phase particles is not effective as a barrier against shear localization in these partially quasicrystallized alloys.

Unusual Room Temperature Ductility of A Zr-Based Bulk Metallic Glass Containing Nanoparticles

Ultrasonic excitation induced nanocrystallization and toughening of Zr<sub>46.75</sub>Cu<sub>46.75</sub>Al<sub>6.5</sub> bulk metallic glass

Thermophysical and Mechanical Properties of Multicomponent Zr37Hf16Ni12.5Cu12.5Al11Co6Nb5 Bulk Glass-Forming Alloy

Thermophysical and Mechanical Properties of Multicomponent Zr37Hf16Ni12.5Cu12.5Al1 1co6nb5 Bulk Glass-Forming Alloy

High temperature deformation behaviors of the Zr 63.36 Cu 14.52 Ni 10.12 Al 12 bulk metallic glass

Relating melting temperature with structure heterogeneity and plasticity of Zr57Cu20Al10Ni8Ag5 bulk metallic glass

Enhanced Plasticity of a Zr50Cu48Al2 Bulk Metallic Glass

Room-Temperature Mechanical Characterization of Bulk Glassy and Partially Crystallized Zr63Al9.7Ni9.7Cu14.6Nb3 Alloys

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Enhanced Plasticity by Introducing Icosahedral Medium-Range Order in Zrcunial Metallic Glass

Unusual Compressive Plasticity of a Centimeter-Diameter Zr-based Bulk Metallic Glass with High Zr Content

Room-Temperature Mechanical Characterization of Bulk Glassy and Partially Crystallized Zr<sub>63</sub>Al<sub>9.7</sub>Ni<sub>9.7</sub>Cu<sub>14.6</sub>Nb<sub>3</sub> Alloys

Enhanced Ductility in a Zr65Cu15Al10Ni10 Bulk Metallic Glass by Nanocrystallization During Compression

A Series of Zr-Based Bulk Metallic Glasses with Room Temperature Plasticity

Significant Room-Temperature Plasticity in a High Zr-containing Bulk Glassy Alloy

High-zirconium Bulk Metallic Glasses with High Strength and Large Ductility

A Plastic Zr–Cu–Ag–Al Bulk Metallic Glass

New type of Zr-Al-Ni-Cu bulk metallic glass with high plasticity at room temperature

Study of mechanical property and crystallization of a ZrCoAl bulk metallic glass

The Coupling Effect of Small Nanocrystals and Free Volume on the Ductility of Cu46Zr47Al7 Bulk Metallic Glass Alloy

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties