Phase Formation, Crystal Structures and Magnetic Properties of Perovskite-Type Phases in the System La2Co1+z(MgxTi1−x)1−zO6
S. Shafeie,J. Grins,S. Ya. Istomin,L. Karvonen,S. A. Chen,T. H. Chen,J. M. Chen,A. Weidenkaff,M. Karppinen,T. Sirtl,G. Svensson
DOI: https://doi.org/10.1016/j.jssc.2010.11.002
IF: 3.3
2011-01-01
Journal of Solid State Chemistry
Abstract:Perovskite-type cobaltates in the system La2Co1+z(MgxTi1−x)1−zO6 were studied for z=0≤x≤0.6 and 0≤x<0.9, using X-ray and neutron powder diffraction, electron diffraction (ED), magnetic susceptibility measurements and X-ray absorption near-edge structure (XANES) spectroscopy. The samples were synthesised using the citrate route in air at 1350°C. The space group symmetry of the structure changes from P21/n via Pbnm to R3¯c with both increasing Mg content and increasing Co content. The La2Co(MgxTi1−x)O6 (z=0) compounds show anti-ferromagnetic couplings of the magnetic moments for the Co below 15K for x=0, 0.1 and 0.2. XANES spectra show for the compositions 0≤x≤0.5 a linear decrease in the L3/(L3+L2) Co–L2,3 edge branching ratio with x, in agreement with a decrease of the average Co ion spin-state, from a high-spin to a lower-spin-state, with decreasing nominal Co2+ ion content.