Ductile Quasicrystalline Alloys

A Inoue,T Zhang,MW Chen,T Sakurai,J Saida,M Matsushita
DOI: https://doi.org/10.1063/1.125907
IF: 4
2000-01-01
Applied Physics Letters
Abstract:An icosahedral (I) quasicrystalline phase with a grain size below 40 nm was formed as a metastable phase in crystallization of the bulk glassy Zr65Al7.5Cu17.5-xNi10Mx (M=Ag, Pd, Au, or Pt; x=5 and 10 at %) alloys. The volume fraction (V-f) of the I phase is about 85% for the 5% M alloy and nearly 100% for the 10% M alloy. The I phase changes to Zr2Cu+Zr2Ni+Zr2Al3 in a fully annealed state. Compressive fracture strength (sigma(c,f)) and fracture elongation (epsilon(c,f)) of the 10% Pd cylinder with a diameter of 2 mm are respectively 1640 MPa and 2.2% for the glassy phase and increase to 1830 MPa and 3.1% for the I phase. The increase in sigma(c,f) is due to the suppression effect of the I particles against the shear deformation of the intergranular glassy phase, and the increase in epsilon(c,f) results from the localization effect of deformation into the glassy layer. The precipitation of the I phase implies that the glassy alloys include randomly oriented I configurations. The present work shows promise for the new class of high-strength nanoquasicrystalline materials. (C) 2000 American Institute of Physics. [S0003-6951(00)00408-3].
What problem does this paper attempt to address?