Structure, Magnetic, and Transport Properties of Ti-substitutedLa0.7Sr0.3MnO3
MS Kim,JB Yang,Q Cai,XD Zhou,WJ James,WB Yelon,PE Parris,D Buddhikot,SK Malik
DOI: https://doi.org/10.1103/physrevb.71.014433
2005-01-01
Abstract:Ti-substituted perovskites La0.7Sr0.3Mn1-xTixO3 with 0less than or equal toxless than or equal to0.20, were investigated by neutron diffraction, magnetization, electric resistivity, and magnetoresistance (MR) measurements. All samples show a rhombohedral structure (space group R(3) over bar c) from 10 K to room temperature. At room temperature, the cell parameters a,c and the unit cell volume increase with increasing Ti content. However, at 10 K, the cell parameter a has a maximum value for x=0.10, and decreases for x>0.10, while the unit cell volume remains nearly constant for x>0.10. The average (Mn,Ti)-O bond length increases up to x=0.15, and the (Mn,Ti)-O-(Mn,Ti) bond angle decreases with increasing Ti content to its minimum value at x=0.15 at room temperature. Below the Curie temperature T-C, the resistance exhibits metallic behavior for the xless than or equal to0.05 samples. A metal (semiconductor) to insulator transition is observed for the xgreater than or equal to0.10 samples. A peak in resistivity appears below T-C for all samples, and shifts to a lower temperature as x increases. The substitution of Mn by Ti decreases the 2p-3d hybridization between O and Mn ions, reduces the bandwidth W, and increases the electron-phonon coupling. Therefore, the T-C shifts to a lower temperature and the resistivity increases with increasing Ti content. A field-induced shift of the resistivity maximum occurs at xless than or equal to0.10. The separation of T-C and the resistivity maximum temperature T-rho,T-max enhances the MR effect in these compounds due to the weak coupling between the magnetic ordering and the resistivity as compared with La0.7Sr0.3MnO3.