Ionic Liquid Gating and Phase Transition Induced Semiconducting to Metallic Transition in La 0.67 Sr 0.33 MnO 3 /BaTiO 3 Heterostructures
Yuchen Wang,Dongxing Zheng,Junwei Zhang,Wanchao Zheng,Ping Wang,Shasha Liu,Chao Jin,Haili Bai
DOI: https://doi.org/10.1021/acsami.0c11910
2020-08-26
Abstract:The strongly correlated La<sub>0.67</sub>Sr<sub>0.33</sub>MnO<sub>3</sub> (LSMO) thin films were deposited on the BaTiO<sub>3</sub> (BTO) substrates to study the influence of temperature-dependent phase transition of BTO on the magnetic and electric transport properties of the LSMO films. Because of the large lattice mismatch between the LSMO and BTO substrates, the ultrathin LSMO film exhibits semiconducting transport behavior rather than the normal metal–insulator transition behavior. A Mn<sup>2+</sup>–O<sup>2–</sup>–Mn<sup>3+</sup> dominated double exchange interaction, which leads to a semiconducting to metallic transition behavior, was formed by the joint effect of the ion-liquid gating and phase transition of the BTO substrates. Our work shows a special way to modulate the conduction mechanism, which opens up a new field for further study of the magnetoelectric coupling of the LSMO/BTO heterostructures.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c11910?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c11910</a>.STEM images of the LSMO/BTO heterostructure, <i>M</i>–<i>H</i> curves for the LSMO/BTO heterostructures at <i>V</i><sub>G</sub> = 0, +3, and −3 V, respectively, d<i>M</i>/d<i>T</i> of the LSMO/BTO heterostructures at <i>V</i><sub>G</sub> = (a) 0, (b) +3, and (c) −3 V, AFM image of the gated LSMO/BTO heterostructure, <i>R</i>–<i>T</i> curves for the LSMO/STO heterostructures at <i>V</i><sub>G</sub> = (a) 0, (b) +3, and (c) −3 V, <i>R</i>–<i>T</i> curves for the LSMO/BTO heterostructures at <i>V</i><sub>G</sub> = (a) 0, (b) +3, and (c) −3 V, XAS at Mn L<sub>3,2</sub> edges for the 5 nm LSMO film (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c11910/suppl_file/am0c11910_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology