Enhanced Electrocaloric Effect in Lead-Free BaTi1−xSnxO3 Ceramics Near Room Temperature

Zhengdong Luo,Dawei Zhang,Yang Liu,Di Zhou,Yonggang Yao,Chenqi Liu,Brahim Dkhil,Xiaobing Ren,Xiaojie Lou

DOI: https://doi.org/10.1063/1.4895615]

IF: 4

2014-01-01

Applied Physics Letters

Abstract:The electrocaloric effect in lead-free BaTi1−xSnxO3 (BTSn, x = 0.08, 0.105, and 0.14) ferroelectric ceramics was studied by using an indirect method. It was found that the largest electrocaloric response could be achieved in BTSn with x = xQP = 0.105 near room temperature with an adiabatic temperature change ΔT of 0.61 K and an electrocaloric strength ΔT/ΔE of 0.31 K mm kV−1, under a modest electric field ΔE of 20 kV cm−1, which is comparable with the best values reported in lead-free materials. These enhanced values are attributed to the multiphase (four phases) coexistence at x = xQP corresponding to the quasi-quadruple point composition.