High Energy Storage Efficiency and Large Electrocaloric Effect in Lead-Free BaTi0.89Sn0.11O3 Ceramic

Soukaina Merselmiz,Zouhair Hanani,Daoud Mezzane,Matjaz Spreitzer,Andraz Bradesko,David Fabijan,Damjan Vengust,Lahoucine Hajji,Zahra Abkhar,Anna Razumnaya,Brigita Rozic,Igor A. Lukyanchuk,Zdravko Kutnjak

DOI: https://doi.org/10.1016/j.ceramint.2020.06.163

2020-11-17

Abstract:Lead-free BaTi0.89Sn0.11O3 (BTSn) ceramic was elaborated via a solid-state reaction method and its dielectric, ferroelectric, energy storage, electromechanical as well as electrocaloric properties were investigated at 25 kV/cm. Pure perovskite structure was confirmed by X-ray diffraction analysis. The maximum of the dielectric constant was found to be 17390 at 41 °C. The enhanced total energy density, the recovered energy density, and the energy storage efficiency of 92.7 mJ/cm3, 84.4 mJ/cm3, and 91.04%, respectively, were observed at 60 °C, whereas the highest storage efficiency of 95.87 % was obtained at 100 °C. At room temperature, the electromechanical strain and the large-signal piezoelectric coefficient reached a maximum of 0.07 % and 280 pm/V. The large electrocaloric effect of 0.71 K and the electrocaloric responsivity of 0.28. 10-6 <a class="link-external link-http" href="http://K.mm/kV" rel="external noopener nofollow">this http URL</a> at 49 °C under 25 kV/cm were indirectly calculated via Maxwell relation from the ferroelectric polarization P (T, E) that was determined from the P-E hysteresis loops. By exploiting the Landau-Ginzburg-Devonshire (LGD) phenomenological theory, the electrocaloric response was estimated to be of 0.61 K at 50 °C under 25 kV/cm. We conclude that BTSn lead-free ceramic is a promising candidate for potential applications in high-efficiency energy storage devices and solid-state refrigeration technology.

Materials Science