Properties of MgB2 Thin Films with Carbon Doping

AV Pogrebnyakov,XX Xi,JM Redwing,V Vaithyanathan,DG Schlom,A Soukiassian,SB Mi,CL Jia,JE Giencke,CB Eom,J Chen,YF Hu,Y Cui,Q Li

DOI: https://doi.org/10.1063/1.1782258

IF: 4

2004-01-01

Applied Physics Letters

Abstract:We have studied structural and superconducting properties of MgB2 thin films doped with carbon during the hybrid physical-chemical vapor deposition process. A carbon-containing precursor metalorganic bis(methylcyclopentadienyl)magnesium was added to the carrier gas to achieve carbon doping. As the amount of carbon in the film increases, the resistivity increases, Tc decreases, and the upper critical field increases dramatically as compared to clean films. The self-field Jc in the carbon doped film is lower than that in the clean film, but Jc remains relatively high to much higher magnetic fields, indicating stronger pinning. Structurally, the doped films are textured with columnar nano-grains and highly resistive amorphous areas at the grain boundaries. The carbon doping approach can be used to produce MgB2 materials for high magnetic-field applications.