Improvement of Critical Current Density and Upper Critical Field in MgB2 using Carbohydrate

J. H. Kim,M. S. A. Hossain,X. Xu,W. K. Yeoh,D. Q. Shi,S. X. Dou,S. Ryu,M. Rindfleisch,M. Tomsic

DOI: https://doi.org/10.48550/arXiv.cond-mat/0612472

2006-12-19

Abstract:We evaluated the doping effects of carbohydrate (malic acid, C4H6O5), from 0wt% to 30wt% of total MgB2, on the phase, lattice parameters, critical temperature, resistivity, and upper critical field of MgB2 superconductor. The lattice parameters calculated show a large decrease in the a-axis for MgB2 + C4H6O5 samples, but no change in the c-axis. This is an indication of the carbon substitution into boron coming from C4H6O5, resulting in enhancement of resistivity, critical current density, and upper critical field. Specifically, the critical current density value of 25000 Acm2 at 5 K and 8 T for the MgB2 + 30wt% C4H6O5 sample is higher than that of the un-doped MgB2 by a factor of 21. In addition, resistivity value for all the MgB2 + C4H6O5 samples ranged from 80 to 90 microohm centimeter at 40 K, which is higher than for un-doped MgB2. The increased resistivity indicates increased impurity scattering due to carbon, resulting in enhanced upper critical field.

Superconductivity

What problem does this paper attempt to address?

This paper aims to study the effects of adding different proportions of malic acid (a carbohydrate with the chemical formula \( \text{C}_4\text{H}_6\text{O}_5 \)) on the phase structure, lattice parameters, critical temperature (\( T_c \)), resistivity (\( \rho \)), upper critical field (\( H_{c2} \)) and other properties of \( \text{MgB}_2 \) superconductors. Specifically, the researchers evaluated the improvement effects of malic acid doping from 0 wt% to 30 wt% on the properties of \( \text{MgB}_2 \) superconductors, especially focusing on how the substitution of boron (B) by carbon (C) affects the resistivity, critical current density (\( J_c \)) and upper critical field (\( H_{c2} \)) of the superconductor. The study found that as the amount of malic acid doping increases, the \( a \)-axis lattice parameter of \( \text{MgB}_2 \) decreases significantly, while the \( c \)-axis remains unchanged, indicating that carbon does enter the \( \text{MgB}_2 \) structure and replaces some boron atoms, thereby enhancing \( \rho \), \( J_c \) and \( H_{c2} \). In particular, in the case of 30 wt% malic acid doping, the \( J_c \) value reaches \( 2.5\times 10^4 \, \text{A/cm}^2 \) at 5 K and 8 T, which is 21 times higher than that of undoped \( \text{MgB}_2 \). In addition, the resistivity of all doped samples at 40 K ranges from 80 to 90 \( \mu \Omega \cdot \text{cm} \), which is higher than that of undoped \( \text{MgB}_2 \). These results show that the performance of \( \text{MgB}_2 \) superconductors can be significantly improved by malic acid doping.