Abstract:Oxygen evolution reaction (OER) is the key anode reaction for electrochemical water splitting, while it is severely hindered by the sluggish rection kinetics and insufficient stability of traditional electrocatalysts. To address the urgent need for efficient and low-cost electrocatalysts, a promising heterogenous CoFe-layered double hydroxide-based electrocatalyst (Ce@CoFe-LDH) is developed by a one-step hydrothermal method combined with rapid electrodeposition. The ultrafine Ce(OH)3 nanoparticles effectively trigger the local surface activity of CoFe-LDH nanowires by the interface electron transfer, thereby promoting the improvement of OER activity and stability. Consequently, the Ce@CoFe-LDH electrocatalyst only needs 207 mV overpotential to obtain 10 mA cm-2, while the Tafel slope is only 50.0 mV dec-1, smaller than those of CoFe-LDH catalyst (232 mV, 74.2 mV dec-1, respectively). Importantly, the Ce@CoFe-LDH exhibits remarkable catalytic durability toward OER at 100 mA cm-2 over 120 hours. First-principles theoretical calculations reveal that interface engineering can be used to optimize the electronic structure of Ce@CoFe-LDH by the charge redistribution and thereby decrease the energy barrier of rate-determining step. In addition, the Ce@CoFe-LDH electrocatalyst as anode for water splitting also shows a low cell potential of 1.47 V at 10 mA cm-2 and robust stability at 100 mA cm-2 over 50 hours. Overall, this work provides new insights into designing efficient OER electrocatalysts for scalable water splitting in clean energy and environmental applications.

Highly Defective CeO2 As a Promoter for Efficient and Stable Water Oxidation

Highly Disordered Fe-Doped CeO 2 with Oxygen Vacancies Facilitates Electrocatalytic Water Oxidation

Highly Defective Fe-Based Oxyhydroxides from Electrochemical Reconstruction for Efficient Oxygen Evolution Catalysis

Defect-Rich NiCeOx Electrocatalyst with Ultrahigh Stability and Low Overpotential for Water Oxidation

Activating Lattice Oxygen by Defect-Engineered Fe2O3-CeO2 Nano-Heterojunction for Efficient Electrochemical Water Oxidation

Ceria‐Optimized Oxygen‐Species Exchange in Hierarchical Bimetallic Hydroxide for Electrocatalytic Water Oxidation

Synergistic Engineering of Dopant and Support of Ru Oxide Catalyst Enables Ultrahigh Performance for Acidic Oxygen Evolution

Boosting Electrocatalytic Oxygen Evolution: Superhydrophilic/Superaerophobic Hierarchical Nanoneedle/Microflower Arrays of Ce x Co3- xO4 with Oxygen Vacancies

Exceptionally active and stable RuO2 with interstitial carbon for water oxidation in acid

Interface-engineered urchin-like CoFe-layered double hydroxide for high-efficiency electrocatalytic oxygen evolution

Boosting Activity and Stability of Electrodeposited Amorphous Ce‐Doped NiFe‐Based Catalyst for Electrochemical Water Oxidation

CeO2 Supported High-Valence Fe Oxide for Highly Active and Stable Water Oxidation

A Dynamically Stable Self-Assembled CoFe (Oxy)hydroxide-Based Nanocatalyst with Boosted Electrocatalytic Performance for Oxygen-Evolution Reaction

Dual-defective-engineered RuO2/D-Co3O4/CC composite as efficient electrocatalysts for triggering oxygen evolution reaction in acidic media

Heterogeneous engineering of nickel-iron sulfide with cerium-promoted reconstruction for enhanced oxygen evolution

Amorphous high-entropy IrRuCrFeCoNiO x as efficient water splitting oxygen evolution reaction electrocatalysts

Self-supported Ru-Fe-Ox nanospheres as efficient electrocatalyst to boost overall water-splitting in acid and alkaline media

Efficient electrocatalysts for OER: Amorphous cerium-doped cobalt sulfide with enhanced performance and durability

Ce Site in Amorphous Iron Oxyhydroxide Nanosheet toward Enhanced Electrochemical Water Oxidation

Breaking the Bottleneck of Activity and Stability of RuO 2 -Based Electrocatalysts for Acidic Oxygen Evolution

Isolated Octahedral Pt-Induced Electron Transfer to Ultralow-Content Ruthenium-Doped Spinel Co3O4 for Enhanced Acidic Overall Water Splitting