Dual-defective-engineered RuO2/D-Co3O4/CC composite as efficient electrocatalysts for triggering oxygen evolution reaction in acidic media

Yujie Liu,Zhaoshuo Yuan,Qi Song,Tongguang Xu,Gang He,Haixiao Sun,Qian Qiao,Xuefeng Guan,Tao Xu,Xiaoping Dai,Xin Zhang

DOI: https://doi.org/10.1007/s40843-023-2734-y

2024-02-04

Science China Materials

Abstract:Defect engineering is widely acknowledged as an effective strategy for improving catalyst performance by increasing the abundance of active sites and optimizing binding energies. Herein, dual-defective-engineered RuO 2 /D-Co 3 O 4 /CC composite was fabricated using a straightforward process involving electrodeposition and acid etching method to improve the oxygen evolution reaction (OER) with low Ru loading (2.42 wt%) in acidic media. The RuO 2 /D-Co 3 O 4 /CC catalyst was thoroughly characterized using physicochemical techniques, revealing the presence of both anionic and cationic defects in RuO 2 /D-Co 3 O 4 /CC. Experimental studies demonstrate that the optimized RuO 2 /D-Co 3 O 4 /CC with dual defects enhances the electrochemically exposed active sites and effectively reduces the dependence of the catalytic reaction on the concentration of protons in the electrolyte, thereby triggering high-performance OER. A mere 181 mV overpotential is needed to achieve a current density of 10 mA cm −2 , and it can sustain uninterrupted continuous electrolysis at this current density for 120 h. This characteristic renders it a highly promising electrocatalyst for acidic OER.

materials science, multidisciplinary