Abstract:In this study, dense anticorrosion magnesium-aluminum layered double hydroxide (MgAl-LDH) films were prepared for the first time by introducing a cationic surfactant tetradecyltrimethyl ammonium bromide (TTAB) in the process of in situ hydrothermal synthesis of Mg-Al LDH films on an AZ31 magnesium alloy. Results of XRD, FTIR, and SEM confirmed that TTAB forms the MgAl-LDH-TTAB, although TTAB cannot enter into LDH layers, and MgAl-LDH-TTAB powders are much smaller and more homogenous than MgAl-CO32--LDH powders. Results of SEM, EDS, mapping, and XPS confirmed that TTAB forms the MgAl-LDH-TTAB films and endows LDH films with denser structure, which provides films with better shielding efficiency. Results of potentiodynamic polarization curves (PDP) and electrochemical impedance spectroscopy (EIS) confirmed that MgAl-LDH-TTABx g films have better corrosion resistance than an MgAl-CO32--LDH film. The corrosion current density (icorr) of the MgAl-LDH-TTAB0.35 g film in 3.5 wt.% NaCl solution was reduced to 1.09 × 10-8 A.cm-2 and the |Z|f = 0.05 Hz value was increased to 4.48 × 105 Ω·cm2. Moreover, the increasing concentration of TTAB in MgAl-LDH-TTABx g (x = 0.025, 0.05, 0.1, 0.2 and 0.35) provided denser outer layer LDH films and thereby increased the corrosion resistance of the AZ31 Mg alloy. Additionally, the |Z|f = 0.05 Hz values of the MgAl-LDH-TTAB0.35 g film still remained at 105 Ω·cm2 after being immersed in 3.5 wt.% NaCl solution for 168 h, implying the good long-term corrosion resistance of MgAl-LDH-TTABx g films. Therefore, introducing cationic surfactant in the process of in situ hydrothermal synthesis can be seen as a novel approach to creating efficient anticorrosion LDH films for Mg alloys.

Influence of Embedded ZnAlCe-NO3− Layered Double Hydroxides on the Anticorrosion Properties of Sol–gel Coatings for Aluminum Alloy

Enhancement of active anticorrosion via Ce-doped Zn-Al layered double hydroxides embedded in sol-gel coatings on aluminum alloy

Duplex Coating Combing Vanadate-Intercalated Layered Double Hydroxide and Ce-Doped Sol–Gel Layers on Aluminum Alloy for Active Corrosion Protection

High corrosion-resistant octanoic acid vapor-phase modified Ce-LDH surface film of aluminum alloy

Sol–gel route to ceria coatings on AA2024-T3 aluminum alloy

Corrosion resistance of anodically oxidized LY12 aluminum alloy after modification with cerium nitrate and silane

Preparation and Corrosion Behaviour of Cerium Based Sol-gel Composite Coatings on AA2024-T4 Aluminum Alloy

Formation of Li-Al LDH conversion layer on AA2024 alloy for corrosion protection

Effect of cerium on the microstructure and anti-corrosion performance of Al-Zn coatings

CeO2-filled sol–gel coatings for corrosion protection of AA2024-T3 aluminium alloy

Corrosion resistance of Mg−Al LDH/Mg(OH)2/silane−Ce hybrid coating on magnesium alloy AZ31

In Situ Growth of High-Performance ZnAl-Layered Double Hydroxides/Al2O3 Composite Coatings on Aluminum Alloy

Superhydrophobic and self-healing silane-ceria composite coating implanted with 1,5-naphthalenediol inhibitor for corrosion protection of AA2024-T3 aluminum alloy

Catechol/m-Phenylenediamine Modified Sol–Gel Coating with Enhanced Long-Lasting Anticorrosion Performance on 3003 Al Alloy

The effect of surface structure on hydrophobicity and corrosion resistance of the MgAlCe-LDH film prepared on the micro-arc oxidation coating of magnesium alloy

Enhanced Corrosion Resistance of Layered Double Hydroxide Films on Mg Alloy: The Key Role of Cationic Surfactant

Active anti-corrosion of epoxy coating by nitrite ions intercalated MgAl LDH

In Situ Preparation of Mg-Al-Co Layered Double Hydroxides on Microarc Oxidation Ceramic Coating of LA103Z Magnesium-Lithium Alloy for Enhanced Corrosion Resistance

Superhydrophobic and Self-Healing Mg-Al Layered Double Hydroxide/Silane Composite Coatings on the Mg Alloy Surface with a Long-Term Anti-corrosion Lifetime

Enhanced corrosion protection of magnesium alloy via in situ Mg–Al LDH coating modified by core–shell structured Zn–Al LDH@ZIF-8

Effect of ZnAl‐LDH on corrosion resistance of Zn–55Al alloy in NaCl solution