In situ study on heavy ion irradiation induced microstructure evolution in single crystal Cu with nanovoids at elevated temperature
Tongjun Niu,Sreekar Rayaprolu,Zhongxia Shang,Tianyi Sun,Cuncai Fan,Yifan Zhang,Chao Shen,Wei-ying Chen,Meimei Li,Yexiang Xue,Haiyan Wang,Anter El-Azab,Xinghang Zhang,Md Nasim
DOI: https://doi.org/10.1016/j.mtcomm.2022.104418
IF: 3.8
2022-09-18
Materials Today Communications
Abstract:Understanding the response of nanovoids to irradiation damage advances our capability to design radiation tolerant materials. Recent in situ studies reveal the shrinkage of hexagon-shaped nanovoids in (110) textured Cu. However, the evolution of voids with irregular geometries under irradiation is less well understood. Here, in situ Kr ion irradiation was performed at 100 °C on single-crystal Cu (112) that possesses nanovoids with high aspect ratio. In situ studies show these elongated voids fragment into smaller voids and shrink gradually with increasing dose. Phase field simulations confirm that fragmentation of the void is governed by the competing kinetics between atoms diffusing toward and away from the elongated nanovoid. Post irradiation analysis reveals the formation of high-density defect clusters.
materials science, multidisciplinary