Abstract:The transparent conductive CuCr1-xNixO2 (0 <= x <= 8%) films were prepared by sol-gel method with two-step annealing process. The structure, morphology, phonon modes, chemical composition, optical bandgap, and electrical properties were systematically studied. It was found that the crystal quality improves first and then decreases with increasing the Ni content, and the inflection point occurs when the doping content is 2% and all samples have the (00l) preferred orientation. In the visible region, the transmittances of these samples range from 75% to 55% as the Ni dopant increases. On the basis of the theoretical calculation, we are inclined to the view that there are two ways of coexisting electronic transitions. The direct band gap decreases from 3.13 to 3.02 eV, and the indirect band gap decreases from 2.78 to 2.49 eV with increasing Ni content. Transmittance spectra of the CuCrO2 film at the temperatures from 323 to 453 K present the fact that the absorption edge shows a slight redshift, which is due to the lattice thermal expansion and the electron-phonon interaction. Raman spectroscopy shows that Ni doping can substitute the Cr sites and further affect Cu-O bonds, which is caused by oxygen deficiency or a relatively smaller crystallite size. Moreover, it suggested that the nonlinear temperature dependence of phonon frequency and line width is a sign of nonharmonic lattice dynamics. The inherent anharmonic force from the crystal results in energy exchange between harmonic phonon normal modes, thereby promoting thermal balance, and in the lattice. The Cu cations have been confirmed to exist in the valence state of Cu1+, and all doped Ni cations exist in a positive divalent state by XPS. Hall effect measurement shows that the conductivities and carrier concentrations of the doped CuCr1-xNixO2 films can be improved by several orders of magnitude larger than that of undoped CuCrO2. The present work suggests that these well crystallized films without a secondary phase can be applied in future p-type optoelectronic devices.

Use of Delafossite Oxides CuCr1-xGaxO2 Nanocrystals in P-Type Dye-Sensitized Solar Cell

Hydrothermal synthesis of ultrasmall CuCrO2 nanocrystal alternatives to NiO nanoparticles in efficient p-type dye-sensitized solar cells

Remarkable Photocurrent Of P-Type Dye-Sensitized Solar Cell Achieved By Size Controlled Cugao2 Nanoplates

Structural, electronic band transition and optoelectronic properties of delafossite CuGa 1-xCr xO 2 (0 ≤ x ≤ 1) solid solution films grown by the sol-gel method

Structural, Electronic Band Transition and Optoelectronic Properties of P-Type Transparent Conductive CuCr1–xNixO2 Semiconductor Films

Interface Modification with CuCrO 2 Nanocrystals for Highly Efficient and Stable Planar Perovskite Solar Cells

Effects of Zn-doping on Structure and Electrical Properties of P-Type Conductive CuCr1−xZnxO2 Delafossite Oxide

Employing surfactant-assisted hydrothermal synthesis to control CuGaO2 nanoparticle formation and improved carrier selectivity of perovskite solar cells

Titanium Dioxide/Calcium Fluoride Nanocrystallite for Efficient Dyesensitized Solar Cell. A Strategy of Enhancing Light Harvest

Bandgap engineering of CuO/TiO 2 nanocomposites and their synergistic effect on the performance of dye-sensitized solar cells

Application of TiO_2 Nanocrystalline to Dye-Sensitized Solar Cells

Facile modified chemical precipitation approach for the synthesis of CuXIn1−XS2 nanocrystals and their application in high-performance CuXIn1−XS2/CdS co-quantum dots sensitized solar cells

Review in optoelectronic properties of p-type CuCrO2 transparent conductive films

Near Field Enhanced Photocurrent Generation in P-Type Dye-Sensitized Solar Cells.

Anatase Tio2 Nanocrystals Enclosed by Well-Defined Crystal Facets and Their Application in Dye-Sensitized Solar Cell

High Photovoltages of CuFeO2 Based P-Type Dye-Sensitized Solar Cells

Cr incorporation in CuGaS2 chalcopyrite: A new intermediate-band photovoltaic material with wide-spectrum solar absorption

Electronic Transition And Electrical Transport Properties Of Delafossite Cucr1-Xmgxo2 (0 <= X <= 12%) Films Prepared By The Sol-Gel Method: A Composition Dependence Study

A highly crystalline Nb3O7F nanostructured photoelectrode: Fabrication and photosensitisation

Controllable Synthesis of Cu2In2ZnS5 Nano/Microcrystals and Hierarchical Films and Applications in Dye-Sensitized Solar Cells

Band Engineering of Ni1−xMgxO Alloys for Photocathodes of High Efficiency Dye-Sensitized Solar Cells