Improving hydrogen storage thermodynamics and kinetics of Ce-Mg-Ni-based alloy by mechanical milling with TiF 3
Hongwei Shang,Wei Zhang,Xin Wei,Yaqin Li,Zeming Yuan,Jun Li,Yanghuan Zhang
DOI: https://doi.org/10.1016/j.jma.2022.09.009
IF: 11.813
2022-10-14
Journal of Magnesium and Alloys
Abstract:Mg-based hydrides are too stable and the kinetics of hydrogen absorption and desorption is not satisfactory. An efficient way to improve these shortcomings is to employ reactive ball milling to synthesize the nanocomposite materials of Mg and additives. In this experiment, TiF 3 was selected as an additive, and the mechanical milling method was employed to prepare the experimental alloys. The alloys used in this experiment were the as-cast Ce 5 Mg 85 Ni 10 , as-milled Ce 5 Mg 85 Ni 10 and Ce 5 Mg 85 Ni 10 + 3 wt.% TiF 3 . The phase transformation, structural evolution, isothermal and non-isothermal hydrogenation and dehydrogenation performances of the alloys were inspected by XRD, SEM, TEM, Sievert apparatus, DSC and TGA. It revealed that nanocrystalline appeared in the as-milled samples. Compared with the as-cast alloy, ball milling made the particle dimension and grain size decrease dramatically and the defect density increase significantly. The addition of TiF 3 made the surface of ball milling alloy particles markedly coarser and more irregular. Ball milling and adding TiF 3 distinctly improved the activation and kinetics of the alloys. Moreover, ball milling along with TiF 3 can decrease the onset dehydrogenation temperature of Mg-based hydrides and slightly ameliorate their thermodynamics.
metallurgy & metallurgical engineering