Abstract:Stabilized Li6.25La3Al0.25 Zr2O12 (cubic LLZO or c-LLZO) is a Li+-conducting ceramic with ionic conductivities approaching 1 mS-cm. Processing c LLZO so that it is suitable for use as a solid state electrolyte in all solid state batteries, however, is challenging due to the formation of secondary phases at elevated temperatures. The work described in this manuscript examines the formation of one such secondary phase La2Zr2O7 (LZO) formed during sintering c LLZO at 1000 °C. Specifically, spatially resolved Raman spectroscopy and X-ray Diffraction (XRD) measurements have identified gradients in Li distributions in the Li ion (Li+)-conducting ceramic Li6.25La3Al0.25 Zr2O12 (cubic LLZO or c-LLZO) created by thermal processing. Sintering c-LLZO under conditions relevant to solid state Li+ electrolyte fabrication conditions lead to Li+ loss and the formation of new phases. Specifically, sintering for 1 h at 1000 °C leads to Li+ depletion and the formation of the pyrochlore lanthanum zirconate (La2Zr2O7 or LZO), a material known to be both electronically and ionically insulating. Circular c-LLZO samples are covered on the top and bottom surfaces, exposing only the 1.6 mm-thick sample perimeter to the furnace's ambient air. Sintered samples show a radially symmetric LZO gradient, with more LZO at the center of the pellet and considerably less LZO at the edges. This profile implies that Li+ diffusion through the material is faster than Li+ loss through volatilization, and that Li+ migration from the center of the sample to the edges is not completely reversible. These conditions lead to a net depletion of Li+ at the sample center. Findings presented in this work suggest new strategies for LLZO processing that will minimize Li+ loss during sintering, leading to a more homogeneous material with more reproducible electrochemical behavior.

Preparation of cubic Li7La3Zr2O12 solid electrolyte using a nano-sized core–shell structured precursor

Preparation of Y-doped Li7La3Zr2O12 by co-precipitation method

Synthesis of Li7La3Zr2O12 Solid Electrolyte by Solid Phase Sintering Method

A novel method for preparation of high dense tetragonal Li7La3Zr2O12

Developing Preparation Craft Platform for Solid Electrolytes Containing Volatile Components: Experimental Study of Competition between Lithium Loss and Densification in Li7La3Zr2O12

Manipulating Li2O atmosphere for sintering dense Li7La3Zr2O12 solid electrolyte

Low temperature synthesis of Al-doped Li7La3Zr2O12 solid electrolyte by a sol–gel process

Submicron-Sized Nb-Doped Lithium Garnet for High Ionic Conductivity Solid Electrolyte and Performance of Quasi-Solid-State Lithium Battery

Nonaqueous Polymer Combustion Synthesis of Cubic Li7La3Zr2O12 Nanopowders

Preparation of high ionic conductivity composite solid electrolyte with in-situ synthesis of LLZO@ZiF-67

Preparation and Electrochemical Properties of Zr-site Substituted Li7La3(Zr2−xMx)O12 (M = Ta, Nb) Solid Electrolytes

Preparation of dense Ta-LLZO/MgO composite Li-ion solid electrolyte: Sintering, microstructure, performance and the role of MgO

A facile method for the synthesis of a sintering dense nano-grained Na 3 Zr 2 Si 2 PO 12 Na + -ion solid-state electrolyte

Preparation and Electrochemical Properties of Bicontinuous Solid Electrolytes Derived from Porous Li 6.4 La 3 Zr 1.4 Ta 0.6 O 12 Incorporated with Succinonitrile

Microwave-assisted solvothermal synthesis of nanostructured Ga-Doped Li7La3Zr2O12 solid electrolyte with enhanced densification and Li-ion conductivity

Crystal Structure and Preparation of Li7La3Zr2O12 (LLZO) Solid-State Electrolyte and Doping Impacts on the Conductivity: An Overview

Microstructure and ion conductivity of Al‐LLZO solid electrolyte prepared by molten salt and cold sintering process

Lithium Volatilization and Phase Changes during Aluminum-Doped Cubic Li6.25La3Zr2Al0.25O12 (c-LLZO) Processing

Key factors of the self-consolidation mechanism for sintering Li7La3Zr2O12 solid electrolytes

Low-Temperature Manufacture of Cubic-Phase Li7La3Zr2O12 Electrolyte for All-Solid-State Batteries by Bed Powder

Synergetic Effect of Li-Ion Concentration and Triple Doping on Ionic Conductivity of Li7La3Zr2O12 Solid Electrolyte