Microstructure and mechanical properties of Mo-free Ti(C,N)-based cermets with Ni– x Cr binders

qingqing yang,weihao xiong,man zhang,bin huang,shan chen

DOI: https://doi.org/10.1016/j.jallcom.2014.11.236

IF: 6.2

2015-01-01

Journal of Alloys and Compounds

Abstract:•The dissolution rate of WC increased when Cr content in binders was 20–30wt.%.•The more Cr content in binders, the thicker grey outer rim of Ti(C,N) grains.•There were often fine white speckles in black cores at 20–30wt.% Cr in binders.•The more Cr content in binders, the higher lattice parameter of binder phase.•Transverse rupture strength reached a peak value when binders contained 20wt.% Cr.