Abstract:Ti(C0.7,N0.3)-Mo2C–Ni cermets are fabricated by powder metallurgy methods. We systematically investigate the microstructure, fracture morphology, crack propagation mechanism, and interface characteristics of Ti(C, N)-based cermets with different Ni binder contents.The increased dissolution of carbides and carbonitrides leads to a large amount of (Mo,Ti)(C,N) solid solution precipitates, which then spontaneously nucleate, resulting in a significant increase in the content of white core-gray rim grains in the cermets with a high binder content. The increased Ni binder largely improves the flexural strength and fracture toughness of the Ti(C,N)-based cermets because of the ductile dispersion toughening. The rim-core interfaces have a superior atomic coherent relationship in all Ti(C,N)-based cermets owing to the small lattice mismatch. The lattice mismatch of the interface between the rim phase and metal binder is remarkably decreased with the increase in the binder content to construct an atomic coherent relationship. Thus, the increased Ni binder promotes atomic ordering at the interface between the ceramic grains and binder and strengthens the grain boundary. The characteristic (111) peak of nickel shifts to a larger angle due to the reduction in the Ni-based solid solution lattice distortion. Therefore, the effect of solid solution strengthening is diminished with the increase in binder content, which results in a decreased binder strength. In the Ti(C,N)-based cermets with low metal binder contents, the fracture of the grain boundary between the ceramic grains and binder is the predominant failure mechanism. The intergranular crack accompanied by crack branching is the main characteristic of crack propagation. A hybrid fracture mode of intergranular and transgranular cracks is observed in the Ti(C,N)-based cermets with a moderate binder content. As the binder content further increases, the plastic yield deformation and subsequent tearing of the metal binder are the main fracture characteristics because of grain boundary strengthening and decreased strength of the binder.

Effect of Mo Addition on Microstructure, Magnetic and Mechanical Properties of TiC-TiN-WC-Ni Cermets

Influence of Mo addition on microstructure and mechanical properties of Ti(C,N)-based cermets fabricated by in-situ carbothermal reduction of TiO2

Experimental Investigation and Thermodynamic Analysis of TiC–Fe Cermets with Mo Additions

Effect of Cr2C3 addition on microstructure and mechanical properties of Ti(CN)-based cermets

Effect of Y2O3 Addition on the Microstructure and Mechanical Properties of TiCN-based Cermets

Effect of Cr<sub>2</sub>C<sub>3</sub> Addition on Microstructure and Mechanical Properties of Ti(CN)-Based Cermets

Effects of nano-TiC substitution on the magnetic properties of Ti(C,N)-based cermets

Effect of Mn addition on the microstructure, interface structure and mechanical properties of MoCoB–Co cermets prepared by in-situ synthesis

Influence of WC content on microstructure and mechanical properties of Mo2FeB2-based cermets fabricated by multi-step sintering

Effects of CrMnFeCoNi additions on microstructure, mechanical properties and wear resistance of Ti(C,N)-based cermets

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets

Effect of C content on the surface gradient structure of (Ti, Mo)(C, N) and Ti(C, N)-based cermets

Fracture Behaviors of Ti(C, N)-based Cermets with Different Contents of Metal Binder

Effect of chemical composition on the microstructure and mechanical properties of MoCoB based cermets

Correlation between microstructure and mechanical properties of Ti(C,N)-xWC-Ni cermets prepared by mechanical activation and subsequent in situ carbothermal reduction

Effect of TiC content on the microstructure and mechanical properties of Ti-30Mo-xTiC composites

The Formation of Ni-Mo Alloy Phase in Ticn-Based Cermets

Microstructure and Properties of Ti(C,N)-Based Cermets with AlxCoCrFeNiTi Binder

Effect of Mo on Microstructures and Wear Properties of In Situ Synthesized Ti(C,N)/Ni-Based Composite Coatings by Laser Cladding