Abstract:Mechanical fracture is commonly regarded as one of key ingredients affecting the reliability of Li-ion battery electrode. In order to avoid the rapid mechanical collapse of electrode, attempts have been made to work on obtaining the accurate critical fracture condition for electrode particle with initial cracks under diffusion-induced stress produced in Li-ion intercalation and deintercalation process. However, considering the integrated fracture process on pristine particle, it is crucial to assess crack initiation phase in fracture analysis so as to obtain the comprehensive failure margins of three-dimensional primary particle. This paper evaluates the diffusion induced stress for NCM primary particle morphology under lithiation-delithiation condition, where the coevolving process of diffusion and stress generation is implemented with both diffusion driven approach and chemical potential driven approach by developing finite element subroutines. Based on the coupled diffusion-stress analyses, crack onset and growth of ternary cathode particle are studied by using ABAQUS extended finite element method (XFEM) with appropriate mesh density and verified by experimental observation. The integrated crack initiation and fracture margins with various current densities and particle dimensions are plotted. The innovative equations to acquire critical particle dimension for crack initiation and fracture under applied electrochemical load are established, which are significant for evaluating particle status. Associating the critical failure diagram with the size distribution of particles in NCM electrode samples, the failure proportion is presented for electrode in microscale. The impact of diffusion on active material property is also investigated comprehensively in stress evolution and fracture analysis.

Cohesive Modeling of Crack Nucleation in a Cylindrical Electrode under Axisymmetric Diffusion Induced Stresses

Cohesive Modeling of Crack Nucleation under Diffusion Induced Stresses in a Thin Strip: Implications on the Critical Size for Flaw Tolerant Battery Electrodes

Three-Dimensional Cohesive Zone Modeling on Interface Crack Initiation from Nanoscale Stress Concentration

The Influence of Stress-Dependent Overpotential on Dendrite Growth in All-Solid-state Battery with Cracks

Crack Nucleation and Growth As Strain Localization in a Virtual-Bond Continuum

Solution of Collinear Cracks in an Electrostrictive Solid

Modeling of inter- and transgranular stress corrosion crack propagation in polycrystalline material by using phase field method

A Coupled Crystal Inelasticity-Phase Field Model for Crack Growth in Polycrystalline Nitinol Microstructures

Can a cylindrical geometry describe diffusion in a nanometric porous media?

A phase field model coupling lithium diffusion and stress evolution with crack propagation and application in lithium ion batteries.

Damage Nucleation During Electromigration along an Isolated Interface in an Elastic Medium

Phase Field Modeling of Chemomechanical Fracture of Intercalation Electrodes: Role of Charging Rate and Dimensionality

Thermo-elastic Cracked Cylindrical Shells and Plates Carrying Non-stationary Electrical Current

Formation of solid-state dendrites under the influence of coherency stresses: A diffuse interface approach

Crack Interaction with Nanoscale Twinning Near a Second-Phase Particle in Fine-Grained Magnesium Alloy

Cohesive Zone Modeling for 3D Ductile Crack Propagation

Strain gradient plasticity-based modeling of hydrogen environment assisted cracking

The Diffusion Induced Stress and Cracking Behaviour of Primary Particle for Li-ion Battery Electrode

Study on Stress Singularities in Cylindrical Shells with an Arbitrary Oriented Crack Using Digital Gradient Sensing Technique

Continuum and Atomistic Models of Strongly Coupled Diffusion, Stress, and Solute Concentration

Two-way coupled modeling of dislocation substructure sensitive crystal plasticity and hydrogen diffusion at the crack tip of FCC single crystals