Abstract:In this study, anatase TiO2 nanostructured films were successfully prepared via Ti foil-assisted hydrothermal synthesis method without any surfactants. With the increase of hydrothermal time from 3 to 12 h, the surface morphologies of the films changed from nanotubes to nanoflowers and the thickness of the films increased from 2.5 to 4.2 mu m. The nanoflowers were seated on a layer of oriented nanotubes and consisted of nanosheets. Both nanotubes and nanosheets were multi-walled, comprising interconnected [TiO6] octahedra. Ti foil and acid-treated Ti foil both formed pieces of thin films on the surface with nanotubes and nanoflowers, respectively. Photoelectrochemistry tests showed that the photocurrent response of the nanotube film was nearly 13.8 mu A/cm(2), which was approximately three times higher than that of nanoflowers film. This indicates that the nanotubes more successfully transferred electrons to the surface of the film as a result of nanotubes providing direct pathways for electrons from the point of injection to the Ti foil electrode. The ultraviolet (UV)-visible-near infrared (NIR) absorption spectra indicated that the nanotube film had a narrower band gap as compared to the nanoflower film. In other words, a relatively low hydrothermal treatment temperature or relatively short hydrothermal treatment time is better for preparing excellent photocurrent response films. (C) 2015 Elsevier B.V. All rights reserved.

CONTROLLABLE HYDROTHERMAL SYNTHESIS AND MORPHOLOGY EVOLUTION OF TiO2 NANOROD FILMS

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Shape Evolution Of Pb (Zr,Ti)O-3 Nanocrystals Under Hydrothermal Conditions

Effect of Key Parameters on the Morphology Transformation of Three-Dimensional TiO2 Solid Microspheres

Hydrothermal synthesis and morphology control mechanism of BaTiO3 from NaTi3O6(OH)(H2O)2 precursors

Morphology Control and Photocatalytic Activity of Tio2 Film

Titanate Nanowire As A Precursor for Facile Morphology Control of Tio2 Catalysts with Enhanced Photocatalytic Activity

Hydrothermal Synthesis of TiO2 Nanostructure Films and Their Photoelectrochemical Properties

Controllable Synthesis of Nanorod/nanodisk TiO 2 from Titanium-Containing Electric Furnace Molten Slag

Hydrothermal synthesis of a dysmorphic double layer structure TiO2 nanorod films and its properties

Controllable Growth of Tio2 Nanopowders by Hydrothermal Synthesis Method

From Titanates to TiO 2 Nanostructures: Controllable Synthesis, Growth Mechanism, and Applications

Controlled Synthesis of Various Morphologies SrTiO3 Nanostructures Via a PVA-assisted Hydrothermal Route

Morphology control and transition of ZnO nanorod arrays by a simple hydrothermal method

Hydrothermal Growth of Well-Aligned TiO2 Nanorod Arrays: Dependence of Morphology Upon Hydrothermal Reaction Conditions

Synthesis and Characterization of TiO_2 Nano-crystalline with Different Morphologies by Low-temperature Hydrothermal Method

Controlling the Synthetic Pathways of Tio2-Derived Nanostructured Materials

Morphology Control of Tio2 Through Hydrothermal Synthesis Method Using Protonic Tetratitanate

Morphology-controlled Synthesis of SrTiO3/TiO2 Heterostructures and Their Photocatalytic Performance for Water Splitting

Novel Synthesis and Property of TiO2 Nano Film Photocatalyst with Mixed Phases