Abstract:Abstract PbZr0.52Ti0.48O3 nanocrystals were synthesized by a hydrothermal method. The effect of NaOH concentration, reaction temperature and time on nucleation and growth of PbZr0.52Ti0.48O3 nanocrystals was investigated. As the 0.05 mol/L PbZr0.52Ti0.48O3 precursors were heated at 200 °C for 21 h with NaOH concentration of 0.5 mol/L, the tetragonal PbZr0.52Ti0.48O3 nanocrystals were formed, and the grain size was more than 20 nm. With increasing the NaOH concentration from 0.5 to 1.5 mol/L, the grain size of PbZr0.52Ti0.48O3 nanocrystals decreased. When the precursors were heated at different temperatures (140 °C to 200 °C) for 21 h with 1.0 mol/L NaOH, single-phase PbZr0.52Ti0.48O3 nanocrystals were obtained at 160 °C to 200 °C. With increasing the reaction temperature from 160 °C to 200 °C, the grains size of PbZr0.52Ti0.48O3 nanocrystals increased from 5 nm to 9 nm. When the precursors were heated at 160 °C in different reaction times from 6 h to 21 h, the evolution from amorphous to crystalline PbZr0.52Ti0.48O3 nanocrystals in correlation with the reaction time was observed. Single crystalline PbZr0.52Ti0.48O3 nanocrystals with narrow size distribution (from 5 nm to 9 nm) were synthesized by controlling the NaOH concentration, reaction temperature and time. The obtained results can find potential application in preparing PbZr0.52Ti0.48O3 thin films on flexible substrates.

Controllable Growth of Tio2 Nanopowders by Hydrothermal Synthesis Method

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Controllable Hydrothermal Synthesis, Optical and Photocatalytic Properties of TiO2 Nanostructures

Control of Microscopic Morphology and Structure of One Dimensional Titanium Dioxide Nanomaterials

Influence of solution concentration on the hydrothermal preparation of titania crystallites

Template-free Hydrothermal Synthesis of Macroporous TiO2 Microspheres on a Large Scale

Facile and large-scale synthesis of hollow TiO2 nanostructures from TiCl3 solution

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Size-controlled synthesis of BaTiO3 nanocrystals via a hydrothermal route

A study on the synthesis of coarse TiO2 powder with controlled particle sizes and morphology via hydrolysis

Direct Continuous Hydrothermal Synthesis of High Surface Area Nanosized Titania

Hydrothermal synthesis and photocatalytic property of CaTiO 3 assisted with sodium citrate

The Influence of TiO2·H2O Gel on Hydrothermal Synthesis of SrTiO3 Powders

pH control on preparation of nano-TiO_2 by gel-sol process

Low-temperature Synthesis of TiB2 Nanocrystals Using TiO2 ,LiBH4 and Mg

From Titanates to TiO 2 Nanostructures:Controllable Synthesis,growth Mechanism,and Applications

Low-temperature Synthesis of Bi4Ti3O12 Nanocrystals by Hydrothermal Method

Effect of Key Parameters on the Morphology Transformation of Three-Dimensional TiO2 Solid Microspheres

Hydrothermal Synthesis of Titania Powder with Different Particle Sizes