Abstract:Phenolic resin was thermally cured on the melamine-based amino foam fiber to construct a nitrogen-containing composite. By employing the composite as the precursor, nitrogen doped microporous carbons were synthesized by two process schemes. One process was two-step of pre-carbonization and further activation (TNC). Another route was one-step of simultaneous activation and carbonization (ONC). Physicochemical properties of resulting carbons were characterized, and super-capacitive performances were also examined. Specific surface area of TNC and ONC were 1657 and 1223 m2 g−1, respectively. The doped nitrogen in the corresponding carbons were determined to be 2.6 and 3.1 at.%. Using the TNC and ONC as electroactive materials, in a three-electrode test configuration in 6.0 M KOH aqueous electrolyte, the electrode harvests the specific capacitance of 316.4 and 303.8 F g−1 at 1.0 A g−1 current density, respectively. When the current density increased to 10 A g−1, retention rates of the corresponding specific capacitance were 88.7 and 85.9%, respectively. In the symmetric-electrode system in aqueous electrolyte, an electrode enclosed the TNC exhibited a specific capacitance of 269.7 F g−1 at the current density of 0.5 A g−1. The assembled simulated supercapacitor delivered an energy density of 9.6 W h kg−1 with the power density of 124.9 W kg−1. The purpose of the present work was to clarify the effect of preparation procedures on the physicochemical properties and super-capacitive performances of porous carbons. Findings demonstrated that the porous carbon prepared by two-step of pre-carbonization and then reactivation showing larger specific surface area and better super-capacitive performance than that of synthesized via one-step of in situ carbonization and activation.

Preparation and Capacitance of Copper-Doped Activated Carbon from Polyacrylonitrile (pan) Precursor

Preparation of Polyaniline Doped with Acid and Polymer Using Electrochemical Deposition

Preparation and Electrochemical Properties of PF-based Activated Carbon

A Novel Strategy to Prepare N, S-codoped Porous Carbons Derived from Barley with High Surface Area for Supercapacitors

Preparation of N-, S-Co-Doped Activated Carbons Derived from Waste Medium Density Fiberboard for Supercapacitors

Cu-modified biomass-derived activated carbons for high performance supercapacitors

A Novel Approach for Preparing In-Situ Nitrogen Doped Carbon Via Pyrolysis of Bean Pulp for Supercapacitors

N-Doped Porous Carbons with High Surface Areas Prepared Through One-Step Chemical Activation and Their Application for Supercapacitors

Nitrogen Doped Microporous Carbons with Tunable and Selective Performances in Supercapacitor and Heterogeneous Catalysis

Polyacrylonitrile As a Binder Realizes High-Rate Activated-Carbon-Based Supercapacitors

High-yield synthesis of N-rich polymer-derived porous carbon with nanorod-like structure and ultrahigh N-doped content for high-performance supercapacitors

N- and O-doped Carbonaceous Nanotubes from Polypyrrole for Potential Application in High-Performance Capacitance

Nitrogen-doped carbon derived from composite of phenolic and amino foam: Effect of synthesis processes on physicochemical properties and super-capacitive performances

Activated Carbon Coated with Polyaniline As an Electrode Material in Supercapacitors

Study on Acidified Carbon Nanotubes Modified Polyacrylonitrile Hollow Fiber Membrane

Activated carbon nanofibers derived from polyimides containing aryl imidazole and hydroxyl groups for high-performance supercapacitors

Design and construction of low resistance copper doped polyaniline electrode with ultrahigh loading density for high performance supercapacitor applications

PREPARATION AND ELECTROCHEMICAL PROPER TIES OF ACTIVATED CARBONS BY KOH ACTIVATION FROM SHENHUA BITUMINOUS COAL

EFFECTS OF PREPARATION PROCESS CONDITIONS ON THE PORE STRUCTURE AND ELECTROCHEMICAL PERFORMANCE OF THE PITCH COKE BASED ACTIVATED CARBON FOR ELECTRIC DOUBLE-LAYER CAPACITORS

Preparation and Electrochemical Properties of Coal-Based Activated Carbons

Microporous and Grain-Sized Design of High-Yield Porous Carbon Materials by Using Potassium Acetate and p -Phenylenediamine