Enhanced mass diffusion phenomena in highly defective doped ceria

vincenzo esposito,de wei ni,zeming he,wei zhang,a s prasad,julie a glasscock,christodoulos chatzichristodoulou,severine ramousse,andreas kaiser
DOI: https://doi.org/10.1016/j.actamat.2013.07.012
IF: 9.4
2013-01-01
Acta Materialia
Abstract:The densification and grain growth of the solid state ionic conductor material Ce0.9Gd0.10O1.95-delta, (i.e. GDC10, gadolinium-doped ceria, with Gd 10 mol.%) are analysed for nanometric and fine powders of various particle sizes, both in air and in a 9 vol.% H-2-N-2 mixture. Due to a dominant solute drag effect in aliovalent highly doped ceria, the starting morphology of the powders controls the diffusion mechanisms of the material in air. Conversely, highly enhanced densification and grain growth are achieved by firing the materials at reduced temperatures (800 < T < 1200 degrees C) in low oxygen activity atmospheres (pO(2) < 10(-1)2 atm). Solute drag is not the rate-limiting step in highly defective GDC and the densification mechanisms are nearly independent of the starting powder properties. Fast diffusion is activated under low oxygen activity with high grain boundary mobility (e.g. M-gb similar to 10(-10) m(3) N-1 s(-1) at 1100 degrees C). The change of the dominant sintering mechanisms under low oxygen activity is attributed to the formation of a large concentration of oxygen vacancies (Vo), electronic defects (Ce'(Ce), i.e. Ce3+) and reduced Gd/Ce cation mismatch. High densification and electric conductivity are achieved in Ce0.9Gd0.1O1.95-delta at low temperatures (similar to 1000 degrees C) and low oxygen activity, preserving the mechanical integrity of the material. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
What problem does this paper attempt to address?