Abstract:The abundance of low-temperature waste heat produced by industry and automobile exhaust necessitates the development of power generation with thermoelectric (TE) materials. Commercially available bismuth telluride-based alloys are generally used near room temperature. Materials that are composed of p-type bismuth telluride, which are suitable for low-temperature power generation (near 380 K), were successfully obtained through Sb-alloying, which suppresses detrimental intrinsic conduction at elevated temperatures by increasing hole concentrations and material band gaps. Furthermore, hot deformation (HD)-induced multi-scale microstructures were successfully realized in the high-performance p-type TE materials. Enhanced textures and donor-like effects all contributed to improved electrical transport properties. Multiple phonon scattering centers, including local nanostructures induced by dynamic recrystallization and high-density lattice defects, significantly reduced the lattice thermal conductivity. These combined effects resulted in observable improvement of ZT over the entire temperature range, with all TE parameters measured along the in-plane direction. The maximum ZT of 1.3 for the hot-deformed Bi0.3Sb1.7Te3 alloy was reached at 380 K, whereas the average ZTav of 1.18 was found in the range of 300–480 K, indicating potential for application in low-temperature TE power generation. Thermoelectric materials, which convert temperature differences and electric voltage into each other, serve in refrigeration or power generation applications. Currently, bismuth telluride (Bi2Te3) and its alloys are the most widely used thermoelectric materials. Tie-Jun Zhu, Xin-Bing Zhao and co-workers from Zhejiang University, China, have now investigated the effect of antimony (Sb) alloying on bismuth tellurides through a series of polycrystalline solid solutions of Bi2-xSbxTe3—where x varies between 1.4 and 1.8—prepared by hot deformation. Systematic tuning of the alloy composition showed that higher antimony content raised the material's optimal conversion temperature by repressing undesirable conduction. This effect arises from an increase in both the hole concentration and the band gap in the material. For a composition where x is 1.7, the alloy showed optimal performances at 380 kelvin—a suitable temperature for low-temperature power generation from the waste heat generated by industry or vehicles. The p-type bismuth telluride-based polycrystalline materials suiting for low-temperature power generations (near 380 K) have been obtained through Sb-alloying and HD, which suppresses the detrimental effect of intrinsic conduction at elevated temperature via increasing the hole concentration and band gap. The hot-deformed Bi0.3Sb1.7Te3 alloy, not usual composition Bi0.5Sb1.5Te3, shows a maximum ZT of 1.3 at 380 K, indicating a bright application potential in low-temperature power generations.

Enhanced Figure of Merit in Antimony Telluride Thermoelectric Materials by In–Ag Co-Alloying for Mid-Temperature Power Generation

Mid-temperature Thermoelectric Performance of Zone-Melted Sb2(Te,Se)3 Alloys Near Phase Transition Boundary

Enhanced thermoelectric performance of n-type bismuth-telluride-based alloys via In alloying and hot deformation for mid-temperature power generation

Shifting Up the Optimum Figure of Merit of P-Type Bismuth Telluride-Based Thermoelectric Materials for Power Generation by Suppressing Intrinsic Conduction

Band convergence and nanostructure modulations lead to high thermoelectric performance in SnPb0.04Te-y% AgSbTe2

Attaining high mid-temperature performance in (Bi,Sb) 2 Te 3 thermoelectric materials via synergistic optimization

Improved Thermoelectric Properties of BiSbTe-AgBiSe 2 Alloys by Suppressing Bipolar Excitation

Enhanced Thermoelectric and Mechanical Performances in Sintered Bi 0.48 Sb 1.52 Te 3 –AgSbSe 2 Composite

Enhanced Thermoelectric and Mechanical Performances in Sintered Bi0.48Sb1.52Te3-AgSbSe2 Composite.

Enhanced mechanical and thermoelectric properties enabled by hierarchical structure in medium-temperature Sb2Te3 based alloys

Dual Alloying Enables High Thermoelectric Performance in AgSbTe2 by Manipulating Carrier Transport Behavior

High‐Efficiency Thermoelectric Module Based on High‐Performance Bi0.42Sb1.58Te3 Materials

Thermoelectric Performance of P-Type Zone-Melted Se-doped Bi 0.5 Sb 1.5 Te 3 Alloys

Enhancing room-temperature thermoelectric performance of n-type Bi2Te3-based alloys via sulfur alloying

High Performance Α-Mgagsb Thermoelectric Materials for Low Temperature Power Generation

Sb2Te3 based alloy with high thermoelectric and mechanical performance for low-temperature energy harvesting

Sb Alloying for Engineering High‐Thermoelectric Zt of CuGaTe2

Enhancing Thermoelectric Performance in P-Type Sb2Te3-Based Compounds Through Nb─Ag Co-Doping with Donor-Like Effect.

Synergistic Suppression of Bipolar Effect and Lattice Thermal Conductivity Leading to High Average Figure of Merit in Bi 0.4 Sb 1.6 Te 3 Materials through Alloying with AgSbTe 2

High Performance BiSbTe Alloy for Superior Thermoelectric Cooling

High-performance Ag0.8Pb18+xSbTe20 Thermoelectric Bulk Materials Fabricated by Mechanical Alloying and Spark Plasma Sintering