Abstract:The Co1−xZnxFe2O4 (Co–Zn) ferrite nanoparticles with x varying from 0.0 to 0.4 have been manufactured by facile chemical co-precipitation method and characterized using structural, morphological, compositional, magnetic and optical properties. XRD pattern revealed that the as-prepared samples have a single-phase spinel structure and good crystallinity which indicate that zinc substitution leads to an increase in both lattice constant and interplanar spacing. FTIR spectra indicate that organic phase annihilation and the spinel phase formation were observed for the prepared sample. The morphological study by SEM shows that the particles have almost spherical grains with narrow size distribution which are appropriate to attain colloidal stability in ferrofluid. The magnetic characterization was studied by VSM which shows that the high cobalt content samples with x < 0.3 show hysteresis, while samples with lower cobalt content show superparamagnetic nature. The saturation magnetization of Zn-substituted cobalt ferrite nanoparticles decreases appreciably with an increase in Zn concentration shown under the hysteresis curve. Low magnetic field ac susceptibility measurement shows a decrease in Curie temperature from 466 to 237 °C with an increase in zinc content of cobalt ferrite. Thus, by adjusting the zinc and cobalt content in an appropriate proportion, sample with superparamagnetic behaviour with required saturation magnetization and desired Curie temperature can be achieved.

A Study of the Magnetic-Properties of Cobalt Ferrite-Coated Zinc Ferrite Particles

Effect of Cobalt-Ferrite Epitaxial Layer on the Coercivity of ZnFe-ferrite Particles (Abstract)

Characterization of ZnO:Co particles prepared by hydrothermal method for room temperature magnetism

Structure And Magnetic Properties Of Co2.73fe0.27o4 Synthesized By The Heat-Decomposition Method

MECHANISM OF HIGHLY COERCIVITY ON EPITAXIAL Co-FERRITES

Variation in Structural Properties and Cation Distribution with Zinc Addition in Cobalt Ferrites

Magnetic Properties of ZnO-doped Cobalt Ferrite

Effect of Zn-substitution on magnetic structure of cobalt ferrite nanoparticles

Study on Preparation and Magnetic Property of (Zn1-Δfeδ) [Coδfe2-Δ]o4 Ferrite Nanoparticles

Ferromagnetic resonance study of (Li_(0.5)F_(0.5))_(0.7-y)Zn_(0.3)Co_yFe_2O_4 ferrites system

Synthesis and influence of Zn substitution on optical and magnetic properties of cobalt ferrite nanoparticles by a polyacrylamide gel route

High Magnetic Performance of Cobalt Ferrite and Anomalous Magnetizing Behavior of Cofe2/Oxide Derived from Ferrite

Studies on the magnetism of cobalt ferrite nanocrystals synthesized by hydrothermal method

Influence of Ti4+-Zn2+ Composite Substitution on the Electromagnetic Properties of Co2Z Hexagonal Ferrites

High frequency magnetic mechanism of Ni-substituted Co2Z hexagonal ferrite

Tuning the Magnetic Behavior of Zinc Ferrite via Cobalt Substitution: A Structural Analysis

Effect of ‘Zn’ substitution on structural, morphological, magnetic and optical properties of Co–Zn ferrite nanoparticles for ferrofluid application

High Frequency Magnetic Properties and Microstructure of NiZn/Co2Z Composite Ferrite Material

Magnetic study of the CaxZn1−xFe2O4 system

Synthesis and Characterization of Core-Shell Structured Bimagnetic Cobalt-Coated Iron Nanoparticles

Study of Structural, Magnetic, and Physical Properties in Nano Cobalt Ferrite by Computational Analysis