Abstract:As a wide band-gap semiconductor，SnO2 films have attracted much attention due to their novel optical and electronic properties. It has been reported that the physical properties can be quite different when the size of SnO2 is reduced to nanometer scale due to the large surface-to-volume ratio and the quantum size effects，which may be applied in many kinds of devices, such as solar cells sensors. etc. It is interesting to study the synthesis of SnO2 nanoparticles and their physics properties. In the present work，a soft chemical technique was used to prepare SnO2 nanoparticles with uniform size and good crystallization in alkalescent solution. The surfactant was added during the preparation process to control the growth and agglomeration of crystal precipitates in the solution. X-ray diffraction spectra and transmission electron microscopy were used to characterize the structures of SnO2 nanoparticles before and after thermal annealing. It was found that the nanocrystalline SnO2 particles can be formed by the present technique and the size is about 4 nm with good crystallinity. With changing the preparation parameters，the size of nanocrystalline SnO2 particles is changed. Post thermal annealing at various temperatures （400—1000 ℃） can promote the crystallization and the size of formed particles was increased with increasing annealing temperature. Optical absorption spectra were used to see the change of the optical properties for samples prepared under different conditions. It was found that the optical band gap is enlarged in nanocrystalline SnO2 particles compared with its bulk counterpart, which can be attributed to the quantum confinement effect. The red-shift of the optical band gap with the particle size supported the quantum size effect. A broad photoluminescence band in the range of 350—750 nm can be detected in the annealed samples and the intensity was significantly enhanced after the thermal annealing. The luminescence peak energy was kept at 390 nm which was independent of the particle size. This luminescence band can be ascribed to the luminescence center associated with the oxygen vacancies on the SnO2 particle surface.

Field Emission and Photoluminescence of SnO2 Nanograss

Synthetic and Effect of Annealing on the Luminescent Properties of Zno Nanowire

Synthesis of Two-Dimensional Micron-Sized Single-Crystalline ZnS Thin Nanosheets and Their Photoluminescence Properties

Photoluminescence Properties of SnO2 Nanowhiskers Grown by Thermal Evaporation

Vacuum Electron Field Emission from Sno2 Nanowhiskers Synthesized by Thermal Evaporation

Growth mechanism and photoluminescence of the SnO_2 nanotwists on thin film and the SnO_2 short nanowires on nanorods

Vacuum Electron Field Emission From Sno2 Nanowhiskers Annealed In N-2 And O-2 Atmospheres

Photoluminescence and Field Emission of 1D ZnO Nanorods Fabricated by Thermal Evaporation

Synthesis and Photoluminescence Properties of Sno2/Zno Hierarchical Nanostructures

Field Emission from in Situ -Grown Vertically Aligned SnO 2 Nanowire Arrays

Hydrothermal Synthesis and Photoluminescence Properties of La2−xEuxSn2O7 (x=0–2.0) Nanocrystals

Electroluminescence of SnO2∕p-Si heterojunction

Facile synthesis of SnO2 nanograss array films by hydrothermal method

Synthesis,structures and Luminescence Properties of SnO2 Nanoparticles

Investigation of Luminescence Properties of ZnO Nanowires at Room Temperature

A Novel Hydrothermal Route to Synthesize Solid SnO 2 Nanospheres and Their Photoluminescence Property

Synthesis and Photoluminescence Properties of String-Like Zno/Sno Nanowire/Nanosheet Nano-Heterostructures

Photoluminescence of SnO2nanoparticles Embedded in Al2O3

Growth Process, Photoluminescence Property and Photocatalytic Activity of SnO<sub>2</sub> Nanorods

Synthesis and Field-Emission of Aligned SnO 2 Nanotubes Arrays

Field Emission from Zinc Oxide Nanostructures and Its Degradation