Abstract:As a wide band-gap semiconductor，SnO2 films have attracted much attention due to their novel optical and electronic properties. It has been reported that the physical properties can be quite different when the size of SnO2 is reduced to nanometer scale due to the large surface-to-volume ratio and the quantum size effects，which may be applied in many kinds of devices, such as solar cells sensors. etc. It is interesting to study the synthesis of SnO2 nanoparticles and their physics properties. In the present work，a soft chemical technique was used to prepare SnO2 nanoparticles with uniform size and good crystallization in alkalescent solution. The surfactant was added during the preparation process to control the growth and agglomeration of crystal precipitates in the solution. X-ray diffraction spectra and transmission electron microscopy were used to characterize the structures of SnO2 nanoparticles before and after thermal annealing. It was found that the nanocrystalline SnO2 particles can be formed by the present technique and the size is about 4 nm with good crystallinity. With changing the preparation parameters，the size of nanocrystalline SnO2 particles is changed. Post thermal annealing at various temperatures （400—1000 ℃） can promote the crystallization and the size of formed particles was increased with increasing annealing temperature. Optical absorption spectra were used to see the change of the optical properties for samples prepared under different conditions. It was found that the optical band gap is enlarged in nanocrystalline SnO2 particles compared with its bulk counterpart, which can be attributed to the quantum confinement effect. The red-shift of the optical band gap with the particle size supported the quantum size effect. A broad photoluminescence band in the range of 350—750 nm can be detected in the annealed samples and the intensity was significantly enhanced after the thermal annealing. The luminescence peak energy was kept at 390 nm which was independent of the particle size. This luminescence band can be ascribed to the luminescence center associated with the oxygen vacancies on the SnO2 particle surface.

Study on Raman Spectra and Photoluminescence of SnO2 Nanowires

Structural, Luminescent, and NO2 Sensing Properties of SnO2-core/V2O5-shell Nanorods

Synthesis and Raman Scattering Study of Rutile Sno2 Nanowires

Study of the Raman-Spectrum of Nanometer Sno2

Photoluminescence Properties of SnO2 Nanowhiskers Grown by Thermal Evaporation

Synthesis,structures and Luminescence Properties of SnO2 Nanoparticles

A Simple Method to Synthesize Single-Crystalline Zn2SnO4(ZTO) Nanowires and Their Photoluminescence Properties

Growth mechanism and photoluminescence of the SnO_2 nanotwists on thin film and the SnO_2 short nanowires on nanorods

Synthesis and characterization of SnO2 nanorods

Growth Process, Photoluminescence Property and Photocatalytic Activity of SnO<sub>2</sub> Nanorods

Study on structural and optical properties of Sn-doped ZnO nanoarrays

Growth of SnO2 nanowires with uniform branched structures

Low-Frequency and Abnormal Raman Spectrum in SnO2 Nanorods

Investigation of Luminescence Properties of ZnO Nanowires at Room Temperature

Preparation of Sno2 Nanowires Synthesized by Vapor-Solid Mode and Its Growth Mechanism

A Novel Hydrothermal Route to Synthesize Solid SnO 2 Nanospheres and Their Photoluminescence Property

Synthesis and optical properties of SnO2 nanorods

Synthesis Structure and Optical Properties of Ag Doped SnO2 Nanowires

Synthesis and Optoelectrical Properties of SnO 2 Nanospheres Derived by Microwave-Assisted Hydrothermal Method

Synthesis of hybrid amorphous/crystalline SnO2 1D nanostructures: investigation of morphology, structure and optical properties

Origin of Low-Temperature Photoluminescence from SnO2 Nanowires Fabricated by Thermal Evaporation and Annealed in Different Ambients