Tunable Emission Properties of Tri-Doped Ca9LiY2/3(PO4)7:Ce3+,Tb3+, Mn2+ Phosphors with Warm White Emitting Based on Energy Transfer
Jindi Wang,Riyan Su,Min Cui,Mengmeng Shang
DOI: https://doi.org/10.1016/j.jre.2020.05.001
IF: 4.632
2020-01-01
Journal of Rare Earths
Abstract:Tri-doped Ca9LiY2/3(PO4)(7):Ce3+,Tb3+,Mn2+ phosphors were prepared by a high-temperature solid state method. Under UV light excitation, Ca9LiY2/3(PO4)(7):Ce3+ samples exhibit a broad band ranging from 320 to 500 nm. At 77 K, the emission spectra of Ca9LiY2/3(PO4)(7):Ce3+ samples present two obvious emission peaks, indicating that Ce3+ ions occupy two different kinds of lattice sites (Ca(1/2) and Ca(3)). As a good sensitizer for Tb3+,Ce3+ ions in Ca9LiY2/3(PO4)(7) lattice can effectively transfer part of energy to Tb3+, and the energy transfer mechanism is determined to be dipole-dipole interaction. Consequently, the emitting color for Ce3+ and Tb3+ co-doped Ca9LiY2/3(PO4)(7) samples can be tuned from bluish violet to green. In order to further enlarge the emission gamut, Mn2+ ions as red emission components were added, forming tri-doped single-phase Ca9LiY2/3(PO4)(7):Ce3+,Tb3+,Mn2+ phosphors. The Ca9LiY2/3(PO4)(7): Ce3+,Tb3+,Mn2+ phosphors exhibit tunable emission properties through controlling the relative doping concentration of Ce3+,Tb3+ and Mn2+. Especially, Ca9LiY2/3(PO4)(7):0.09Ce(3+),0.12 Tb3+, 0.30Mn(2+) can emit warm white light. The sample shows good thermal stability. At 150 degrees C, the emission intensity for Ce3+ (360 nm), Tb3+ (545 nm) and Mn2+ (655 nm) decreases to 63%, 69%, and 72% of its initial intensity, respectively. Moreover, the sample obtains good stability after 10 cycles between room temperature and 150 degrees C. (C) 2020 Chinese Society of Rare Earths. Published by Elsevier B.V. All rights reserved.