Abstract:Magnetostrictive alloys with a wide operating temperature range from −80 to 150°C were developed by changing the Tb/Dy ratio of TbxDy1−xFe2 from 0.3/0.7 to 0.36/0.64 and Co partly substituting for Fe. The structure, Curie temperature, AC susceptibility, magnetization, magnetocrystalline anisotropy constant K1 and magnetostriction of Tb0.36Dy0.64(Fe1−yCoy)2 (y=0.0, 0.1, 0.2) alloys were investigated. It was found that the matrix of Tb0.36Dy0.64(Fe1−yCoy)2 alloys keeps the MgCu2-type cubic Laves structure with a small amount of R-rich phase. A small amount of R2(Fe,Co) phase was also detected when y=0.2. The Curie temperature Tc of Tb0.36Dy0.64(Fe1−yCoy)2 alloys is higher than Tb0.3Dy0.7Fe2 and increases drastically with increasing Co content from 387.1°C for Tb0.36Dy0.64Fe2 to 416.7°C for Tb0.36Dy0.64(Fe0.9Co0.1)2 and 433.3°C for Tb0.36Dy0.64(Fe0.8Co0.2)2. The spin reorientation temperature Tr decreases from −12°C for Tb0.3Dy0.7Fe2 to −94°C for Tb0.36Dy0.64Fe2. It increases slightly with increasing Co content. The magnetocrystalline anisotropy coefficient K1 of Tb0.36Dy0.64(Fe1−yCoy)2 alloys is greater than Tb0.3Dy0.7Fe2 but decreases with increasing Co content. The saturation magnetization Ms of Co-doped alloys is lower than that of Tb0.3Dy0.7Fe2 and decreases with increasing Co content. The magnetostriction of Tb0.3Dy0.7Fe2 and Tb0.36Dy0.64(Fe1−yCoy)2 alloys was examined against applied magnetic field up to 5kOe in the temperature range from −80 to 150°C.The temperature coefficient of magnetostriction (Δλ/ΔT) of Tb0.3Dy0.7Fe2 and Tb0.36Dy0.64(Fe1−yCoy)2 alloys was also calculated by linearly simulating the magnetostriction-temperature curve, showing that the absolute value of Δλ/ΔT at 5kOe magnetic field is 1.17 ppm/°C for y=0.1 and 1.35 ppm/°C for y=0.2, smaller than that of Co free samples, which is 2.43ppm/°C for Tb0.36Dy0.64Fe2.

New Fe-Based Amorphous Alloys with Large Magnetostriction and Wide Supercooled Liquid Region Before Crystallization

High-temperature Magnetic Properties of Fe-based Nanocrystalline Alloy

Synthesis and Properties of Ferromagnetic Fe-based (fe, Ni, Co)–Mo–P–C–B Bulk Metallic Glasses with Large Supercooled Liquid Region

Ductile Fe-Based Amorphous Alloys with High Iron Content

Preparation of FeCo-based amorphous alloys with excellent soft magnetism and high glass transition temperature

Nanocrystallization, good soft magnetic properties and ultrahigh mechanical strength for Fe82-85B13-16Si1Cu1 amorphous alloys

Fe-based Bulk Amorphous Alloys with High Glass Formation Ability and High Saturation Magnetization

Glass-Forming Ability, Crystallized Structure and Magnetic Properties of Fe67co9.5nd3dy0.5b20 Glassy Alloy with Large Supercooled Liquid Region

Fe-B-Si-C-Cu amorphous and nanocrystalline alloys with ultrahigh hardness and enhanced soft magnetic properties

Magnetic Properties of Amorphous Nd2(Fe1−xCox)23

Development of high Bs Fe–Ni-based metal amorphous nanocomposite by optimization of glass-forming ability

Thermal and magnetic properties of Fe(Co)BCCu amorphous alloys with high saturation magnetization of 1.77 T

Novel Tin-Containing Fe-Base Glassy Alloys

Soft magnetic properties of Co-doped FeSiBC amorphous and nanocrystalline alloys

Amorphous-crystalline Transition Layers Formation During Quenching of Fe61 Co7 Zr10 Mo5 W2B15 Melt

Two-stage-like Glass Transition and the Glass-Forming Ability of a Soft Magnetic Fe-based Glassy Alloy

Magnetic Properties and Glass-Forming Ability of Modified Fe–P–Si–B Bulk Amorphous Alloys

The Co-Doped Tb0.36dy0.64fe2 Magnetostrictive Alloys with A Wide Operating Temperature Range

Liquid state properties and amorphous solidification kinetics of multicomponent alloys investigated under containerless processing conditions

Mechanically Alloyed Multi-Component Mo-based Amorphous Alloys with Wide Supercooled Liquid Region

Tunable magnetocaloric effect in amorphous Gd-Fe-Co-Al-Si alloys