Obtaining Extremely Low Coercivity of High Bs FeCoBSiCPCu Nanocrystalline Alloys Through Modulation of Magnetic Anisotropy
Mingjuan Cai,Zhijun Guo,Lei Li,Xingyu Zheng,Xiaoxuan Yang,Qianqian Liu,Gaopeng Zou,Baolong Shen
DOI: https://doi.org/10.1016/j.jmst.2024.04.047
2025-01-01
Abstract:Longitudinal magnetic field annealing is utilized for modifying the magnetic anisotropy and enhancing the magnetic softness of Fe 75 Co 8 (B 10 Si 3 C 3 P 1 ) 1- x /17 Cu x ( x = 0.5, 0.75, 1, 1.25) nanocrystalline alloys. All of the magnetic field -annealed nanocrystalline alloys with Cu content more than 0.5 at.% exhibit significantly improved soft -magnetic properties, including high saturation magnetic flux density up to 1.87 T, effective permeability of 13,0 0 0-16,0 0 0 under the condition of 1 A/m and 1 kHz, coercivity as low as 1.6 A/m, and core loss of 0.11-0.45 W/kg under the condition of 1.0 T and 50 Hz. The application of a magnetic field promotes the nucleation and inhibits the growth of grains, leading to an increase in the number density of nanocrystals and the crystalline volume fraction, and a reduction in the grain size. The magnetic field annealing reduces the effective magneto -crystalline anisotropy energy to 2-4 J/m 3 , and induces longitudinal magnetic anisotropy with anisotropy energy density of 40 0-90 0 J/m 3 which shows dependence on the crystalline volume fraction. The field -induced magnetic anisotropy dominates over the random local magnetic anisotropies, and results in the formation of regular magnetic domains aligned longitudinally, pinning -free domain wall displacement, and thus enhanced soft -magnetic properties. (c) 2024 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.