Effect of Magnetic Field Annealing on Microstructure and Magnetic Properties of FeCuNbSiB Nanocrystalline Magnetic Core with High Inductance
Xingdu Fan,Fangliang Zhu,Qianqian Wang,Mufeng Jiang,Baolong Shen
DOI: https://doi.org/10.9729/am.2017.47.1.29
2017-01-01
Applied Microscopy
Abstract:Since the nanocrystalline Fe73.5Si13.5B9Nb3Cu1 alloy was first found by Yoshizawa in 1988, nanocrystalline soft magnetic alloys (Makino, 2012; Ohta & Yoshizawa, 2008; Suzuki et al., 1991a, 1991b; Willard et al., 1998) have attracted great attention due to their excellent soft magnetic properties such as high saturation magnetic flux density (Bs), high initial permeability (μi), low coercivity (Hc) and low core loss (P). From then on, three typical nanocrystalline alloy systems have been developed under the trade name of Finemet (Hitachi Matels Ltd., Japan) (Yoshizawa et al., 1988), Nanoperm (MH&W International Corp., USA) (Suzuki et al., 1991a, 1991b) and Hitperm (Carnegie Mellon University, USA) (Willard et al., 1998). Among these alloys, Nanoperm exhibits high Bs of 1.5~1.7 T but contains expensive and easily oxidized elements (e.g. Zr or Hf). Hitperm possesses high Curie temperature but the Hc is up to 200 A/m and the large amount of additive element Co increases material cost. Compared to the above alloys, Finemet exhibits high μi of 100,000, low Hc of 0.53 A/m, as well as convenient production process, thus has been widely applied in electronic components such as transformers, inductors, sensors, filters etc. The soft magnetic properties of nanocrystalline alloys result from the uniform nanocrystal structure which effectively reduces the magneto-crystalline anisotropy (Herzer, 1990, 1992, 1997, 2005, 2013). In addition, it has been pointed out that magnetic field annealing can further optimize soft