Ultra-high Heating Rate Densification of Nanocrystalline Magnesia at High Pressure and Investigation on Densification Mechanisms

Jianghao Liu,Zhengyi Fu,Weimin Wang,Jinyong Zhang,Hao Wang,Yucheng Wang,Soowohn Lee,Koichi Niihara

DOI: https://doi.org/10.1016/j.jeurceramsoc.2014.04.004

IF: 5.7

2014-01-01

Journal of the European Ceramic Society

Abstract:The pressure-assisted densification method based on combustion reaction heating was applied to prepare dense nanocrystalline ceramics. The densification process of magnesia compact with a particle size of 50nm was investigated, under the pressure range of 0–170MPa, and the temperature range of 1620–1880K with ultra-high heating rate (above 1600K/min). The pressure was found to have an effect on enhancing densification while suppressing grain growth, and the higher sintering temperature lead to the larger grain size and lower density of the compact. Pure magnesia nanocrystalline ceramics with a relative density of 99.1% was obtained at 1620K and 170MPa, and the concurrent grain growth was almost completely restrained. Furthermore, the investigation on the pressure-dependent densification mechanisms including plastic flow, diffusion and power-law creep was also carried out. The result indicated the rate-controlling mechanism was the plastic flow accommodated by grain-boundary diffusion creep.