Microwave Dielectric Properties of Pb2MoO5 Ceramic with Ultra-Low Sintering Temperature

Huidong Xie,Haihong Xi,Fei Li,Chao Chen,Xiaochang Wang,Di Zhou

DOI: https://doi.org/10.1016/j.jeurceramsoc.2014.05.004

IF: 5.7

2014-01-01

Journal of the European Ceramic Society

Abstract:Ultra-low firing microwave dielectric ceramic Pb2MoO5 with monoclinic structure was prepared via a conventional solid state reaction method. The sintering temperature ranged from 530°C to 650°C. The relative densities of the ceramic samples were about 97% when the sintering temperature was greater than 570°C. The best microwave dielectric properties were obtained in the ceramic sintered at 610°C for 2h with a permittivity ∼19.1, a Q×f value about 21,960GHz (at 7.461GHz) and a temperature coefficient value of −60ppm/°C. From the X-ray diffraction, backscattered electron image results of the co-fired samples with 30wt% silver and aluminum additive, the Pb2MoO5 ceramics were found not to react with Ag and Al at 610°C for 4h. The microwave dielectric properties and ultra-low sintering temperature of Pb2MoO5 ceramic make it a promising candidate for low temperature co-fired ceramic applications.