Abstract:We report the synthesis of hybrid thin films based on polymethyl methacrylate) (PMMA) and polystyrene (PS) doped with 1%, 3%, 5%, and 7% of cerium dioxide nanoparticles (CeO2 NPs). The As-prepared thin films of (PMMA-PS) incorporated with CeO2 NPs are deposited on a glass substrate. The transmittance T% (λ) and reflectance R% (λ) of PMMA-PS/CeO2 NPs thin films are measured at room temperature in the spectral range (250–700) nm. High transmittance of 87% is observed in the low-energy regions. However, transmittance decreases sharply to a vanishing value in the high-energy region. In addition, as the CeO2 NPs concentration is increased, a red shift of the absorption edge is clearly observed suggesting a considerable decrease in the band gap energy of PMMA-PS/CeO2 NPs thin film. The optical constants (n and k) and related key optical and optoelectronic parameters of PMMA-PS/Ce NPs thin films are reported and interpreted. Furthermore, Tauc and Urbach models are employed to elucidate optical behavior and calculate the band gaps of the as-synthesized nanocomposite thin films. The optical band gap energy of PMMA-PS thin film is found to be 4.03 eV. Optical band gap engineering is found to be possible upon introducing CeO2 NPs into PMMA-PS polymeric thin films as demonstrated clearly by the continuous decrease of optical band gap upon increasing CeO2 content. Fourier-transform infrared spectroscopy (FTIR) analysis is conducted to identify the major vibrational modes of the nanocomposite. The peak at 541.42 cm−1 is assigned to Ce–O and indicates the incorporation of CeO2 NPs into the copolymers matrices. There were drastic changes to the width and intensity of the vibrational bands of PMMA-PS upon addition of CeO2 NPs. To examine the chemical and thermal stability, thermogravimetric (TGA) thermograms are measured. We found that (PMMA-PVA)/CeO2 NPs nanocomposite thin films are thermally stable below 110 °C. Therefore, they could be key candidate materials for a wide range of scaled multifunctional smart optical and optoelectronic devices.

Preparation and Characterization of Polysiloxane@CeO 2 @PMMA Hybrid Nano/Microspheres via In Situ One-Pot Process

Co-Continuous Polymeric Nanostructures Via Simple Melt Mixing of Ps/Pmma

Fumed Silica/polymer Hybrid Nanoparticles Prepared by Redox-Initiated Graft Polymerization in Emulsions

Preparation and Morphology of SiO 2 /PMMA Nanohybrids by Microemulsion Polymerization

Preparation and Characterization of Silica/Pmma Composites with Highly Dispersed Silica Nanoparticles Dispersion of Nanosilica in Mma

Encapsulation of silica nanoparticles by redox-initiated graft polymerization from the surface of silica nanoparticles.

Preparation of Polystyrene/Sio2 Composite Nanoparticles Bearing Sulfonic Groups on the Surface Via Emulsion Copolymerization Using A Polymerizable Emulsifier

Preparation of acrylate polymer/silica nanocomposite particles with high silica encapsulation efficiency via miniemulsion polymerization

Preparation of Poly (methyl Methacrylate)/nanometer Calcium Carbonate Composite by In-Situ Emulsion Polymerization

Preparation of SiO2/PMMA Composite Particles Via Conventional Emulsion Polymerization

Synthesis and Properties of Nanosilica‐reinforced Polyurethane for Grouting

A Novel Preparation Method Of Raspberry-Like Pmma/Sio2 Hybrid Microspheres

Synthesis, Optical, Chemical and Thermal Characterizations of PMMA-PS/CeO2 Nanoparticles Thin Film

Facile Synthesis of Poly(methyl methacrylate) Silica Nanocomposite Monolith by In Situ Free Radical Polymerization of Methyl Methacrylate in the Presence of Functionalized Silica Nanoparticles

Synthesis and characterization of PMMA/Al2O3 composite particles by in situ emulsion polymerization

Biomimic preparation of highly dispersible silica nanoparticles based polymer nanocomposites

Synthesis and Characterization of Raspberry-Like Pmma/Sio2 Organic-Inoragnic Composite Particles

Synthesis of UV-Cured Silicone Resin/Silica Nanocomposites from UV-Curable Polysilisiquioxane and Methacrylate-Functionalized Silica

Preparation of Nebula-like Polysiloxane/Silica Superhydrophobic Composite Microspheres Controlled by Density Method

Research of the Synthesis and Film Performance of Silica/poly(st-Ba-mps) Core-Shell Latexes Obtained by Miniemulsion Co-Polymerization

Synthesis and Film Performances of SiO2/P(MMA-BA) Core–shell Structural Latex