Effect of Molding Process on Properties of Laminated Zrb2-Sic-C-G Ultra High Temperature Ceramics

Chuncheng Wei,Xinghong Zhang,Wenbo Han,Ping Hu

DOI: https://doi.org/10.4028/www.scientific.net/kem.602-603.443

2014-01-01

Abstract:Laminated ZrB2- SiC-Cg ceramics were successfully prepared by tape casting -dipping and tape casting -stacking respectively. The effect of different molding process on the mechanical properties of materials was investigated. The microstructure and fracture behavior were characterized as well. The flexural strength, fracture toughness and fracture work of laminated ZrB2-SiC-Cg ceramics prepared by tape casting-stacking were 427 MPa, 11.3 MPa center dot m 1/ 2, 415 J/ m 2, respectively. The thickness of ZrB2-SiC layers was about 250 mu m, and the thickness of graphite layers was about 25 mu m. As a comparison, Laminated ZrB2-SiC-Cg ceramics prepared by tape casting -dipping showed non-uniform thickness of the ZrB2-SiC layers and graphite layers. And the flexural strength, fracture toughness and fracture work of laminated ZrB2-SiC-Cg ceramics prepared by tape casting-dipping were 252 MPa, 5.7 MPa center dot m 1/ 2, 104 J/ m 2, respectively. The improvement on the mechanical properties of laminated ZrB2-SiC-Cg ceramics prepared by tape casting -stacking was attributed to the uniform graphite layer and ZrB2-SiC layer and the reducing amount of graphite infiltrated into ZrB2-SiC matrix layer.