Dielectric Properties and Microstructure of Y-Al-Ga-Si Co-Doped Barium Titanate Ceramics

min jia wang,qi long zhang,xin hui zhao,hui yang

DOI: https://doi.org/10.4028/www.scientific.net/KEM.602-603.700

2014-01-01

Key Engineering Materials

Abstract:Multilayer ceramic capacitors (MLCC) are important functional components of electronic information technology. The development of AC MLCC requires low dielectric loss and high AC breakdown voltage. In this paper, Y-Al-Ga-Si co-doped barium titanate ceramics were prepared by conventional solid state method. Microstructures, surface morphology and dielectric properties were investigated by XRD, SEM, and LCR analyzer, respectively. Y3+ entered into the lattice of BaTiO3, replaced A-sites and B-sites, suppressed grain growth effectively, and made crystal structure change from tetragonal to pseudo-cubic, which reduced dielectric loss and lowered the Curie peak. The sintering characteristic and permittivity can be improved by the incorporation of Al and Ga. BaTiO3 -0.06Y(2)O(3) - 0.02Ga(2)O(3) -0.01Al(2)O(3) -0.01SiO(2) ceramics sintered at 1380 degrees C achieved good dielectric properties: epsilon(r)= similar to 2223, tan delta =similar to 1.1% (at 1kHz), Delta C/C-25 <similar to 15.26% (from -55 degrees C to 150 degrees C).