Abstract:Revealing the microstructural parameters-mechanical properties relationship is very critical for the microstructure tailoring and properties optimization of titanium alloy. In this work, the dependence of mechanical properties on microstructural parameters of TA15 titanium alloy with tri-modal microstructure was investigated. The results indicate that at a certain lamellar α (αl) content (28%), both of yield strength (σ0.2) and ultimate tensile strength (σb) decrease continuously with the increase of equiaxed α (αp) content, while the decrease speed slows down at higher αp content. At a certain content of αp of 20%, σ0.2 and σb both increase first and then decrease as the content of αl increases. The above effect laws result from the competition between the softening effect caused by increasing the softer αp and αl contents and the strengthening effect relating to αl/βt interfaces and βt hardening. As for the elongation (δ) and reduction of area (Φ), they show an increase trend with αp content increasing at a certain αl content of 28%. However, they decrease first and then increase with αl content increasing at a certain αp content of 20%. The early plasticity decrease at lower αl content is due to the popular rapid void nucleation and cleavage fracture along αl/βt interfaces. When αp or αl content increases to higher level, the deformation compatibility and homogeneity improves, which suppress the rapid void nucleation and cleavage fracture along αl/βt interfaces. Meanwhile, the fracture mechanism changes from the coexistence of void coalescence and cleavage fracture to the void coalescence dominated fracture, thus the plasticity increases. Moreover, a back-propagation neural network model was developed to correlate the mechanical properties with microstructural parameters of tri-modal microstructure. The prediction results suggest that better combination of strength and plasticity can be achieved by controlling the contents of αp and αl in the range of 10–15% and 22–27%, respectively.

Tri-modal Microstructure Evolution of TA15 Ti-alloy under Conventional Forging Combined with Given Subsequent Heat Treatment

Tri‐Modal Microstructure Evolution in Near‐β and Two Phase Field Heat Treatments of Conventionally Forged TA15 Ti‐Alloy

Tri-modal Microstructure and Performance of TA15 Ti-alloy under Near-Β Forging and Given Subsequent Solution and Aging Treatment

Tri-modal Microstructure in High Temperature Toughening and Low Temperature Strengthening Treatments of Near-Β Forged TA15 Ti-alloy

Tri-modal Microstructure in Different Loading Zones Under TA15 Ti-alloy Isothermal Local Conventional Forging and Given Subsequent Heat Treatment

Dependence of Microstructure on Solution and Aging Treatment for Near-β Forged TA15 Ti-Alloy

Microstructure evolution of different loading zones during TA15 alloy multi-cycle isothermal local forging

Allowable Ranges of Conventional Forging Parameters Determination for TA15 Ti-Alloy to Obtain Tri-modal Microstructure under Given Subsequent Heat Treatment

Formation and Evolution of Tri-Modal Microstructure During Dual Heat Treatment for TA15 Ti-alloy

Evaluation of Subsequent Heat Treatment Routes for Near-β Forged TA15 Ti-Alloy

Evolution Mechanism of Lamellar alpha in Tr-Modal Microstructure of TA15 Ti-Alloy during Near beta Deformation

Dependence of Mechanical Properties on the Microstructural Parameters of TA15 Titanium Alloy with Tri-Modal Microstructure

Development of Microstructural Inhomogeneity in Multi-Pass Flow Forming of TA15 Alloy Cylindrical Parts

Feasibility analysis of obtaining tri-modal microstructure by multi-pass conventional forging combined with dual heat treatment for near-α titanium alloy with different initial microstructures

Microstructure evolution in the local loading forming of TA15 titanium alloy under non-isothermal condition

Microstructural features of TA15 titanium alloy under different temperature routes in isothermal local loading forming

Parameter Matching of Near- Forging plus Solution and Aging Treatment for Near- Titanium Alloy with Tri-modal Microstructure

Study on Hot Deformation Behavior of TA15 Titanium Alloys During Multi-step Conventional Isothermal Local Forging

Study on High-Temperature Flow Behavior and Substructure and Texture Evolution of TA15 Titanium Alloy

Microstructure and Mechanical Behavior of Heat-Treated and Thermomechanically Processed TA15 Ti Alloy Composites

Prediction and Control of Equiaxed Α in Near-Β Forging of TA15 Ti-alloy Based on BP Neural Network: for Purpose of Tri-Modal Microstructure