Abstract:This study focused on the numerical simulation of the distribution of residual stress in yttria-stabilized zirconia (YSZ) coatings prepared with atmospheric plasma spraying (APS). We particularly investigated the stress distribution around the interface between the top coat and bond coat. During thermal spray deposition, droplets and particles deposit on the substrate in a complex manner, causing interface waviness and non-uniform stress distribution. Therefore, residual stress is an important consideration when preparing thermal barrier coatings (TBCs). Residual stresses directly affect the performance of bond coats (BCs) and ceramic top coats (TCs). To accurately evaluate residual stress, we considered interface waviness and the thickness of the ceramic top coat and conducted a detailed analysis of stress distribution. The results show that compressive stress exists at the TC/BC interface, which may be caused by the mismatch in the thermal expansion coefficient between the YSZ top coat and the substrate, potentially leading to coating delamination. Moreover, the residual stress at the TC/BC interface significantly increases with an increasing YSZ thickness. When the top-coat thickness exceeds 300 μm, stress concentration and failure of the coating are likely to occur. Meanwhile, the optimized thermal spray experiment results confirm that the residual stress at the BC/YSZ interface of the thermal barrier coating is tensile stress, with a maximum value of 155 MPa, which is consistent with the finite element calculation results. Furthermore, the failure modes of TBCs with rough interface conditions are discussed in detail. Our research provides important guidance for TBC design and optimizing their performance.

Evolution of residual stress in air plasma sprayed yttria stabilised zirconia thermal barrier coatings after isothermal treatment

Effects of Residual Stress on the Mechanical Properties of Plasma-Sprayed Thermal Barrier Coatings

Stress Analysis and Failure Mechanisms of Plasma-Sprayed Thermal Barrier Coatings

Phase Transformation Behavior in Air Plasma Sprayed Yttria Stabilized Zirconia Coating

Microstructural evolution of plasma spray physical vapor deposited thermal barrier coatings at 1150 °C studied by impedance spectroscopy

High Temperature Mechanical Properties of Zirconia Metastable T '-Phase Degraded Yttria Stabilized Zirconia

Thermal‐cycle Dependent Residual Stress Within the Crack‐susceptible Zone in Thermal Barrier Coating System

Analysis of thermal shock performance of Y2O3 stabilized ZrO2 (YSZ) coating based on residual stress and micro-morphology

On the oxygen vacancy annealing in air plasma sprayed YSZ thermal barrier coatings

Residual stress evolution of 8YSZ:Eu coating during thermal cycling studied by Eu3+ photoluminescence piezo-spectroscopy

Evolution of Residual Stresses in PS-PVD Thermal Barrier Coatings on Thermal Cycling

Microstructure and Surface Residual Stress of Plasma Sprayed Nanostructured and Conventional ZrO2‐8wt%Y2O3 Thermal Barrier Coatings

Effect of Top-Coat Thickness and Interface Fluctuation on the Residual Stress in APS-TBCs

Constrained Healing and Morphology Change Mechanism of 2D Cracks in Plasma Sprayed Thermal Barrier Coatings

Thermal Aging Behavior of Axial Suspension Plasma-Sprayed Yttria-Stabilized Zirconia (YSZ) Thermal Barrier Coatings

Strain-induced Multiscale Structural Changes in Lamellar Thermal Barrier Coatings

Sintering and Failure Behaviour of Eb-Pvd Thermal Barrier Coating after Isothermal Treatment

Effect of Isothermal Heat Treatment on Plasma‐Sprayed Yttria‐Stabilized Zirconia Studied by Impedance Spectroscopy

High Temperature Fracture Toughness and Residual Stress in Thermal Barrier Coatings Evaluated by an In-Situ Indentation Method

Failure Analysis of Fine-Lamellar Structured Ysz Based Thermal Barrier Coatings with Submicro/Nano-Grains

Thermal Stability of Plasma-Sprayed Thick Thermal Barrier Coatings Using Triplex ProTM-200 Torch