Abstract:1. Srx(Zr0.9Y0.05Yb0.05)O1.95+x‐NiCoCrAlY thermal barrier coatings (TBCs) [SZYY‐1, x = 1.0; SZYY‐2, x = 0.9; SZYY‐3, x = 0.8] were deposited by suspension plasma spraying (SPS) using the corresponding precursors suspension prepared by co‐precipitation. 2. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of 1121°C‐1 h high‐temperature thermal cycling, up to 345 times. 3. The effects of microstructure and phase composition on thermal cycling failure of the coating at high temperatures were studied in detail. A finite element model was also proposed to evaluate the thermal stress thermally grown oxide (TGO) morphology of a real coating at different thermal cycling stages. The thermal barrier coatings (TBCs) consisting of Srx(Zr0.9Y0.05Yb0.05)O1.95+x were prepared using the suspension plasma spraying (SPS) method. Precursor suspensions were prepared via co‐precipitation for this purpose. Detailed microstructural, phase composition, and phase content analyses were conducted on these coatings, designated as SZYY‐1 (x = 1.0), SZYY‐2 (x = 0.9), and SZYY‐3 (x = 0.8). Additionally, the coatings underwent a thermal cycling test at 1121°C for 1 h. To assess the morphology of thermally grown oxide (TGO) in a real coating, a finite element model was employed. SPS‐SZYY‐2 with columnar crystal structure was found to have the highest number of thermal cycling, up to 345 times. The thermophysical high‐temperature properties of the coating can be effectively improved through suitable second‐phase content. Microstructural and finite element analyses revealed that stress, primarily caused by the continuous growth of the Co3O4, NiO and Spinel (CNS) layer within TGO, was the predominant factor leading to coating failure. At elevated temperatures, transverse cracks formed at the interface between the bond coating and ceramic top coating due to mismatched thermal expansion and sintering effects, ultimately leading to coating degradation. Therefore, reducing the generation rate of large stresses in the coating, especially shear stresses, can effectively prevent the generation and propagation of transverse cracks and increase the thermal cycling life of TBCs.

Thermal‐cycle Dependent Residual Stress Within the Crack‐susceptible Zone in Thermal Barrier Coating System

Residual stress evolution of 8YSZ:Eu coating during thermal cycling studied by Eu3+ photoluminescence piezo-spectroscopy

Residual Stress Inspection by Eu3+ Photoluminescence Piezo-Spectroscopy: an Application in Thermal Barrier Coatings

EBSD analysis of microstructure changes in YSZ coatings during thermal cycling

Failure behaviour of EB-PVD YSZ thermal barrier coatings under simulated aero-engine operating conditions

High Temperature Fracture Toughness and Residual Stress in Thermal Barrier Coatings Evaluated by an In-Situ Indentation Method

Analysis of thermal shock performance of Y2O3 stabilized ZrO2 (YSZ) coating based on residual stress and micro-morphology

Prediction of critical rupture of plasma-sprayed yttria stabilized zirconia thermal barrier coatings under burner rig test via finite element simulation and in-situ acoustic emission technique

Effect of Top-Coat Thickness and Interface Fluctuation on the Residual Stress in APS-TBCs

Thickness-related failure behaviors of the thermal barrier coatings under thermal gradient cycling

SEM-Guided Finite Element Simulation of Thermal Stresses in Multilayered Suspension Plasma-Sprayed TBCs

Residual Stress Measurement of Thermal Barrier Coatings

THz-TDS characterization of stress evolution of EB-PVD TBCs under thermal cycling

Thermal cycling behavior of Srx(Zr0.9Y0.05Yb0.05)O1.95+x thermal barrier coatings by suspension plasma spraying

Interface failure behavior of YSZ thermal barrier coatings during thermal shock

Investigation of microstructure changes in Al2O3-YSZ coatings and YSZ coatings and their effect on thermal cycle life

Phase Transformation Behavior in Air Plasma Sprayed Yttria Stabilized Zirconia Coating

OS13F106 Progress of the Residual Stress Measuring Techniques of Thermal Barrier Coatings

Performance of 2024 aluminum alloy thermal barrier coating systems subjected to elevated temperature fluctuation as a fatigue

The effect of hydrothermal corrosion on the phase stability, microstructure and thermal cycling behavior of n-YSZ coating

Thermal Stability of Plasma-Sprayed Thick Thermal Barrier Coatings Using Triplex ProTM-200 Torch